kiểm tra phá hủy mối hàn

kiểm tra phá hủy mối hàn

CÁC PHÉP THỬ CƠ TÍNH CƠ BẢN

Th ử uốn

T hử kéo

Th ử va đập

T hử phá hủy mẫu hàn góc

Tensile Specimen

Fracture Fillet Specimen

CTOD Specimen

Các mẫu thử cơ tính

Thử uốn

Root bend

Face bend

Weld dressed flush

Support Former (4t)

Defect indication

Generally this specimen

would be unacceptable

Face bend

Side bend

Root bend

Minor ruptures on tension surface Acceptance depends upon code

requirements

Thử uốn

Th ử kéo

Transverse Tensile

Specimen

All-Weld Metal Tensile

Specimen

Th ử kéo ngang

Reduced section specimen

None reduced section specimen

Thử va đập

Charpy test piece Anvil

Dial Calibrated

in joules

Hammer

Point

reached

after

fracture

Hammer blow

55

10 10

45 o

2mm

Root radius 0.25mm

100% giòn

10 mm

22 I/2 o

Machined notch

100% mềm

Machined notch

Large reduction

in area, shear lips

Fracture surface 100% bright crystalline brittle fracture

Randomly torn, dull gray

fracture surface

Thử va đập

Thử phá hủy mẫu hàn góc

Hammer

2mm Notch

Thử Macro

Weld Metal HAZ

Parent Metal

Báo cáo thử Macro

DEFECT TYPE

1 Lack of sidewall fusion + slag

2 Slag inclusion

3 Lack of sidewall fusion

4 Cap undercut

DEFECT SIZE

4mm 3.5mm 5.8mm depth 0.6mm

ACCEPT/REJECT

Reject Reject Reject Accept

Sample Number MSR-1189

1

2 3 4