Handbook of Comparative World Steel Standards Part 4 pps

4.1 Carbon Steels for Pressure Vessel Plates 4.1A Mechanical Properties of Carbon Steels for Pressure Vessel Plates Continued Section Thickness Yield Strength, min Tensile Strength, min

Trang 1

4.1 Carbon Steels for Pressure Vessel Plates

4.1A Mechanical Properties of Carbon Steels for Pressure Vessel Plates (Continued)

Section Thickness Yield Strength, min Tensile Strength, min Standard

Designation Grade, Class, Type, Symbol or Name Number Steel Number UNS Treatment Heat t, mm t, in N/mm 2 or

Trang 2

4.1A Mechanical Properties of Carbon Steels for Pressure Vessel Plates (Continued)

Trang 3

4.1B Chemical Composition of Carbon Steel Pressure Plates

Section Thickness Weight, %, Maximum, Unless Otherwise Specified Standard

Designation

Grade, Class, Type, Symbol,

PH 235 - - - - 0.17 0.40-1.20 0.35 0.035 0.030 0.30 0.30 0.08

Cu 0.30; Al ≥ 0.020; Cr+Cu+Mo+Ni 0.70

EN 10028-3:2003 P275NH 1.0487 - - - 0.16 0.80-1.50 0.40 0.025 0.015 0.30 0.30 0.08

Cu 0.30; Nb 0.05; Ti 0.03;

V 0.05; N 0.012; Al ≥ 0.020; Nb+Ti+V 0.05; Cr+Cu+Mo0.45

50 < t ≤ 200 - 0.30 0.90 0.15-0.30 0.035 0.040 - - - -

≤ 12.5 - 0.21 0.85-1.20 0.15-0.40 0.030 0.030 - - - - 12.5 < t ≤ 50 - 0.23 0.85-1.20 0.15-0.40 0.030 0.030 - - - -

50 < t ≤ 100 - 0.25 0.85-1.20 0.15-0.40 0.030 0.030 - - - - JIS G 3118:2000 SGV410 - -

100 < t ≤ 200 - 0.27 0.85-1.20 0.15-0.40 0.030 0.030 - - - -

EN 10028-2:2003 P265GH 1.0425 - - - 0.20 0.80-1.40 0.40 0.025 0.015 0.30 0.30 0.08

Cu 0.30; Nb 0.020; Ti 0.03;

V 0.02; Al ≥ 0.020; N 0.012; Cr+Cu+Mo+Ni 0.70 ISO 9328-2:1991 P 265

PH 265 - - - - 0.20 0.50-1.40 0.35 0.035 0.030 0.30 0.30 0.08

Cu 0.30; Al ≥ 0.020; Cr+Cu+Mo+Ni 0.70

≤ 25 ≤ 1 0.24 0.90 0.15-0.40 0.035 0.035 - - - -

25 < t ≤ 50 1 < t ≤ 2 0.27 0.90 0.15-0.40 0.035 0.035 - - - -

50 < t ≤ 100 2 < t ≤ 4 0.29 0.90 0.15-0.40 0.035 0.035 - - - -

100 < t ≤ 200 4 < t ≤ 8 0.31 0.90 0.15-0.40 0.035 0.035 - - - - ASTM A 515/A 515M-03 60 [415] - K02401

> 200 > 8 0.31 0.90 0.15-0.40 0.035 0.035 - - - -

≤ 12.5 ≤ ½ 0.21 0.60-0.90 0.15-0.40 0.035 0.035 - - - - 12.5 < t ≤ 50 ½ < t ≤ 2 0.23 0.85-1.20 0.15-0.40 0.035 0.035 - - - -

50 < t ≤ 100 2 < t ≤ 4 0.25 0.85-1.20 0.15-0.40 0.035 0.035 - - - -

100 < t ≤ 200 4 < t ≤ 8 0.27 0.85-1.20 0.15-0.40 0.035 0.035 - - - - ASTM A 516/A 516M-03 60 [415] - K02100

> 200 > 8 0.27 0.85-1.20 0.15-0.40 0.035 0.035 - - - -

P 315 TN

PH 315 TN - - - - 0.18 0.70-1.50 0.10-0.40 0.035 0.035 ISO 9328-4:1991

PL 315 TN - - - - 0.16 0.70-1.50 0.10-0.40 0.030 0.030

0.30 0.30 0.08

Cu 0.30; Nb 0.05; Ti 0.03;

V 0.05; N 0.020; Al ≥ 0.020; Nb+Ti+V 0.05; Cr+Cu+Mo 0.45

Trang 4

4.1B Chemical Composition of Carbon Steel Pressure Plates (Continued)

Designation

> 200 > 8 0.33 0.90 0.15-0.40 0.035 0.035 - - - -

≤ 12.5 ≤ ½ 0.24 0.85-1.20 0.15-0.40 0.035 0.035 - - - - 12.5 < t ≤ 50 ½ < t ≤ 2 0.26 0.85-1.20 0.15-0.40 0.035 0.035 - - - -

50 < t ≤ 100 2 < t ≤ 4 0.28 0.85-1.20 0.15-0.40 0.035 0.035 - - - -

100 < t ≤ 200 4 < t ≤ 8 0.29 0.85-1.20 0.15-0.40 0.035 0.035 - - - - ASTM A 516/A 516M-03 65 [450] - K02403

> 200 > 8 0.29 0.85-1.20 0.15-0.40 0.035 0.035 - - - -

25 < t ≤ 50 - 0.31 0.90 0.15-0.30 0.035 0.040 - - - - JIS G 3103:1987 SB 450 - -

50 < t ≤ 100 - 0.33 0.90 0.15-0.40 0.035 0.040 - - - -

≤ 12.5 - 0.24 0.85-1.20 0.15-0.40 0.030 0.030 - - - - 12.5 < t ≤ 50 - 0.26 0.85-1.20 0.15-0.40 0.030 0.030 - - - -

50 < t ≤ 100 - 0.28 0.85-1.20 0.15-0.40 0.030 0.030 - - - - JIS G 3118:2000 SGV450 - -

100 < t ≤ 200 - 0.29 0.85-1.20 0.15-0.40 0.030 0.030 - - - -

EN 10028-2:2003 P295GH 1.0481 - - - 0.08-0.20 0.90-1.50 0.40 0.025 0.015 0.30 0.30 0.08

Cu 0.30; Nb 0.020; Ti 0.03;

V 0.02; Al ≥ 0.020; N 0.012; Cr+Cu+Mo+Ni 0.70

ISO 9328-2:1991

PH 290 - - - - 0.14-0.20 0.90-1.50 0.40 0.035 0.030 0.30 0.30 0.08

Cu 0.30; Al ≥ 0.020; Cr+Cu+Mo+Ni 0.70

25 < t ≤ 50 - 0.33 0.90 0.15-0.30 0.035 0.040 - - - - JIS G 3103:1987 SB 480 - -

50 < t ≤ 200 - 0.35 0.90 0.15-0.30 0.035 0.040 - - - -

Trang 5

Designation

> 200 > 8 0.35 1.20 0.15-0.40 0.035 0.035 - - - -

≤ 12.5 ≤ ½ 0.27 0.85-1.20 0.15-0.40 0.035 0.035 - - - - 12.5 < t ≤ 50 ½ < t ≤ 2 0.28 0.85-1.20 0.15-0.40 0.035 0.035 - - - -

50 < t ≤ 100 2 < t ≤ 4 0.30 0.85-1.20 0.15-0.40 0.035 0.035 - - - -

100 < t ≤ 200 4 < t ≤ 8 0.31 0.85-1.20 0.15-0.40 0.035 0.035 - - - - ASTM A 516/A 516M-03 70 [485] - K02700

> 200 > 8 0.31 0.85-1.20 0.15-0.40 0.035 0.035 - - - -

≤ 40 ≤ 1½ 0.70-1.35ASTM A 537/A 537M-95 (2000) 1 - K12437

> 40 > 1½ 0.24 1.00-1.60 0.15-0.50 0.035 0.035 0.25 0.25 0.08 Cu 0.35 ASTM A 737/A 737M-99 B - K12001 - - 0.20 1.15-1.50 0.15-0.50 0.035 0.030 - - - Cb 0.05

P 315 - - - - 0.20 ISO 9328-2:1991

PH 315 - - - - 0.15-0.20 0.90-1.60 0.10-0.50 0.035 0.030 0.30 0.30 0.08

Cu 0.30; Al ≥ 0.020; Cr+Cu+Mo+Ni 0.70

Trang 6

Designation

P 355 - - - - 0.22 0.90-1.60 0.10-0.50 0.035 0.030 0.30 0.30 0.08 Al 0.020; Cu 0.30 ISO 9328-2:1991

PH 355 - - - - 0.15-0.22 0.90-1.60 0.10-0.50 0.035 0.030 0.30 0.30 0.08 Al 0.020; Cu 0.30

≤ 65 ≤ 2½ 0.24 1.50 0.15-0.50 0.035 0.035 0.25 0.50 0.08 Cu 0.35; V 0.07; Cb 0.04;

Cb+V 0.08 ASTM A 738/A 738M-03a A - K12447

> 65 > 2½ 0.24 1.60 0.15-0.50 0.035 0.035 0.25 0.50 0.08 Cu 0.35; V 0.07; Cb 0.04;

Cb+V 0.08 JIS G 3115:2000 SPV 355 - - - - 0.20 1.60 0.15-0.55 0.030 0.030 - - - -

≤ 40 ≤ 1½ 0.70-1.35

2 - K12437

> 40 > 1½ 0.24 1.00-1.60 0.15-0.50 0.035 0.035 0.25 0.25 0.08 Cu 0.35

≤ 40 ≤ 1½ 0.70-1.35ASTM A 537/A 537M-95 (2000)

3 - K12437

> 40 > 1½ 0.24 1.00-1.60 0.15-0.50 0.035 0.035 0.25 0.25 0.08 Cu 0.35 ASTM A 737/A 737M-99 C - K12202 - - 0.22 1.15-1.50 0.10-0.55 0.035 0.030 - - - V 0.04-0.11; N 0.03

> 65 > 2½ 0.20 0.90-1.60 0.15-0.55 0.030 0.030 0.30 0.60 0.30

Cu 0.35; V 0.07; Cb 0.04; Cb+V 0.08

Trang 7

4.2 Carbon Steels for Pressure Vessel Plates - With Impact Testing Below -20°C

4.2A Mechanical Properties of Carbon Steels for Pressure Vessel Plates - With Impact Testing Below -20°C

Trang 8

4.2A Mechanical Properties of Carbon Steels for Pressure Vessel Plates - With Impact Testing Below -20°C (Continued)

1.0562 1.0565 1.0566 1.1106

P 355 TN

PH 355 TN

PL 355 TN PLH 355 TN

> 65 > 2½ 380 55 515-655 75-95 22 20 J at -40°C

Trang 9

4.2B Chemical Composition of Carbon Steels for Pressure Vessel Plates - With Impact Testing Below -20°C

Designation

SLA 235 A,B - - 6 ≤ t ≤ 50 - 0.15 0.70-1.50 0.15-0.30 0.030 0.025 - - - - JIS G 3126:2000

SLA 325 A,B - - 6 ≤ t ≤ 32 - 0.16 0.80-1.60 0.15-0.55 0.030 0.025 - - - -

Trang 10

4.2B Chemical Composition of Carbon Steels for Pressure Vessel Plates - With Impact Testing Below -20°C

Designation

or Name

Steel

B - K02203 - - 0.19 0.85-1.50 0.15-0.40 0.035 0.035 - - - - ASTM A 662/A 662M-03

P 355 TN

ISO 9328-4:1991

PL 355 TN PLH 355 TN - - - - 0.18

C, Class 2 - -

> 40 > 1½ 0.10 1.00-1.60 0.15-0.50 0.030 0.015 0.25 0.25 0.08

Cu 0.35; V 0.06; Cb 0.06;

Ti 0.006-0.02

Trang 11

4.3 ½Mo Alloy Steels for Pressure Vessel Plates

4.3A Chemical Composition of ½Mo Alloy Steels for Pressure Vessel Plates

Designation

or Name

Steel

EN 10028-2:2003 16Mo3 1.5415 - - - 0.12-0.20 0.40-0.90 0.35 0.025 0.010 0.30 0.30 0.25-0.35 N 0.012; Cu 0.30; Al/N>2 ISO 9328-2:1991 16 Mo 3 - - - - 0.12-0.20 0.40-0.90 0.35 0.035 0.030 0.30 - 0.25-0.35 Cu 0.30

EN 10028-2:2003 18MnMo4-5 1.5414 - - - 0.20 0.90-1.50 0.40 0.015 0.005 0.30 0.30 0.45-0.60 N 0.012; Cu 0.30

≤ 25 ≤ 1 0.18

25 < t ≤ 50 1 < t ≤ 2 0.21

50 < t ≤ 100 2 < t ≤ 4 0.23 ASTM A 204/A 204M-03 A - K11820

> 100 > 4 0.28

0.90 0.15-0.40 0.035 0.035 - - 0.45-0.60 -

≤ 25 ≤ 1 0.20

25 < t ≤ 50 1 < t ≤ 2 0.23 ASTM A 302/A 302M-03 A - K12021

> 50 > 2 0.25

0.95-1.30 0.15-0.40 0.035 0.035 - - 0.45-0.60 -

25 < t ≤ 50 - 0.23 JIS G 3119:1987 SBV 1 A - -

50 < t ≤ 150 - 0.25

0.95-1.30 0.15-0.30 0.035 0.040 - - 0.45-0.60 -

JIS G 3124:1987 SEV 295 - - 6 ≤ t ≤ 150 - 0.19 0.80-1.60 0.15-0.60 0.035 0.035 - - 0.10-0.40 Cu 0.35; Nb 0.05; V 0.10

Trang 12

4.3A Chemical Composition of ½Mo Alloy Steels for Pressure Vessel Plates (Continued)

Designation

50 < t ≤ 150 - 0.25

1.15-1.50 0.15-0.30 0.035 0.040 - - 0.45-0.60 -

≤ 25 ≤ 1 0.20

25 < t ≤ 50 1 < t ≤ 2 0.23 ASTM A 302/A 302M-03 B - K12022

Type A, Class 2 ASTM

A 533/A 533M-93 (1999) Type A,

Class 3

- K12521 - - 0.25 1.15-1.50 0.15-0.40 0.035 0.035 - - 0.45-0.60 -

Trang 13

4.3B Mechanical Properties of ½Mo Alloy Steels for Pressure Vessel Plates

or P

125 < t ≤ 150 - 380 - 520-670 -

19 31 J at 0°C

Trang 14

4.3B Mechanical Properties of ½Mo Alloy Steels for Pressure Vessel Plates

50 < t ≤ 100 - 430 - 590-740 -

100 < t ≤ 125 - 420 - 580-730 - JIS G 3124:1987 SEV 345 - - R, N, NT

Type A, Class 3 - K12521 QT 6.5 < t ≤ 65 0.25 < t ≤ 2½ 570 83 690-860 100-125 16 -

Trang 15

4.4 Cr-Mo Alloy Steels for Pressure Vessel Plates

4.4.1A Chemical Composition of ¾Cr-½Mo Alloy Steels for Pressure Vessel Plates

Designation

or Name

Steel

ASTM A 387/A 387M-03 Grade 2

Class 1 - K12143 - - 0.05-0.21 0.55-0.80 0.15-0.40 0.035 0.035 0.50-0.80 - 0.45-0.60 - SCMV 1 Div 1 - - - - 0.21 0.55-0.80 0.40 0.030 0.030 0.50-0.80 - 0.45-0.60 - JIS G 4109:1987

SCMV 1 Div 2 - - - - 0.21 0.55-0.80 0.40 0.030 0.030 0.50-0.80 - 0.45-0.60 - ASTM A 387/A 387M-03 Grade 2

Class 2 - K12143 - - 0.05-0.21 0.55-0.80 0.15-0.40 0.035 0.035 0.50-0.80 - 0.45-0.60 -

4.4.1B Mechanical Properties of ¾Cr-½Mo Alloy Steels for Pressure Vessel Plates

Designation

Grade, Class, Type, Symbol or Name

Steel Number

UNS Number

Heat Treatment t, mm t, in N/mm 2 or

Trang 16

4.4.2A Chemical Composition of 1Cr-½Mo Alloy Steels for Pressure Vessel Plates

Designation

or Name

Steel

ASTM A 387/A 387M-03 Grade 12

Class 1 - K11757 - - 0.05-0.17 0.40-0.65 0.15-0.40 0.035 0.035 0.80-1.15 - 0.45-0.60 - JIS G 4109:1987 SCMV 2 Div 1 - - - - 0.17 0.40-0.65 0.40 0.030 0.030 0.80-1.15 - 0.45-0.60 -

ASTM A 387/A 387M-03 Grade 12,

Class 2 - K11757 - - 0.05-0.17 0.40-0.65 0.15-0.40 0.035 0.035 0.80-1.15 - 0.45-0.60 - JIS G 4109:1987 SCMV 2 Div 2 - - - - 0.17 0.40-0.65 0.40 0.030 0.030 0.80-1.15 - 0.45-0.60 -

EN 10028-2:2003 13CrMo4-5 1.7335 - - - 0.08-0.18 0.40-1.00 0.35 0.025 0.010 0.70-1.15 - 0.40-0.60 Cu 0.30; N 0.012

ISO 9328-2:1991 14 CrMo 4 5 - - - - 0.08-0.18 0.40-1.00 0.35 0.035 0.030 0.70-1.15 - 0.40-0.60 Cu 0.30

4.4.2B Mechanical Properties of 1Cr-½Mo Alloy Steels for Pressure Vessel Plates

Designation

Steel Number

UNS Number

Trang 17

4.4.3A Chemical Composition of 1¼Cr-½Mo Alloy Steels for Pressure Vessel Plates

Designation

4.4.3B Mechanical Properties of 1¼Cr-½Mo Alloy Steels for Pressure Vessel Plates

Designation

Steel Number

UNS Number

Trang 18

4.4.4A Chemical Composition of 2¼Cr-1Mo Alloy Steels for Pressure Vessel Plates

Designation

0.10 0.30-0.60 0.50 0.035 0.035 2.00-2.50 - 0.90-1.10 -

EN 10028-2:2003 10CrMo9-10 1.7380 - - - 0.08-0.14 0.40-0.80 0.50 0.020 0.010 2.00-2.50 - 0.90-1.10 Cu 0.30; N 0.012 ISO 9328-2:1991 13 CrMo 9 10 T1 - - - - 0.08-0.15 0.40-0.70 0.50 0.035 0.030 2.00-2.50 - 0.90-1.10 Cu 0.30

ASTM A 387/A 387M-03 Grade 22,

Class 2 - K21590 - - 0.05-0.15 0.30-0.60 0.50 0.035 0.035 2.00-2.50 - 0.90-1.10 - JIS G 4109:1987 SCMV 4 Div 2 - - - - 0.17 0.30-0.60 0.50 0.030 0.030 2.00-2.50 - 0.90-1.10 -

ISO 9328-2:1991 13 CrMo 9 10 T2 - - - - 0.08-0.15 0.40-0.70 0.50 0.035 0.030 2.00-2.50 - 0.90-1.10 Cu 0.30

JIS G 4110:1993 SCMQ4E - - - - 0.17 0.30-0.60 0.50 0.015 0.015 2.00-2.50 - 0.90-1.10 V 0.03

Trang 19

4.4.4B Mechanical Properties of 2¼Cr-1Mo Alloy Steels for Pressure Vessel Plates

60 < t ≤ 100 -

310 - 520-670 -

17 27 J at 20°C

Trang 20

4.4.5A Chemical Composition of 3Cr-1Mo Alloy Steels for Pressure Vessel Plates

Designation

0.05-0.05

0.30-0.60 0.50 0.035 0.035 2.75-3.25 - 0.90-1.10 -

JIS G 4109:1987 SCMV 5 Div 2 - - - - 0.17 0.30-0.60 0.50 0.030 0.030 2.75-3.25 - 0.90-1.10 -

4.4.5B Mechanical Properties of 3Cr-1Mo Alloy Steels for Pressure Vessel Plates

Tiêu đề	Handbook of Comparative World Steel Standards Part 4 pps
Trường học	University of Example
Chuyên ngành	Materials Engineering
Thể loại	handbook

Định dạng
Số trang	40
Dung lượng	255,84 KB