Handbook of Comparative World Steel Standards Part 11 ppsx

8.1.4B Mechanical Properties of Precipitation-Hardening Stainless Steels Continued Thickness Yield Strength, min Tensile Strength, min Standard Designation Grade, Class, Type, Symbol o

Trang 1

8.1.4B Mechanical Properties of Precipitation-Hardening Stainless Steels (Continued)

Thickness Yield Strength, min Tensile Strength, min Standard

Designation Grade, Class, Type, Symbol or Name Number Steel Number UNS Heat Treatment Product Form/ t, mm t, in N/mm 2

or MPa ksi N/mm

2 or MPa ksi

Elongation, min, % Hardness, max HB/HRC/HV

Trang 2

or MPa ksi N/mm

2 or MPa ksi

t < 0.25 t < 0.010 450 65 1035 150 - -

Pl, Sh, St/

S 0.25 ≤ t < 102 0.010 ≤ t < 4.0 380 55 1035 150 20 -/92 HRB/ -

0.038 ≤ t < 0.127 0.0015 ≤ t < 0.0050 1035 150 1240 180 - -/38/ - 0.127 ≤ t < 0.25 0.0050 ≤ t < 0.0010 1035 150 1240 180 - -/38/ - 0.25 ≤ t < 0.51 0.010 ≤ t < 0.020 1035 150 1240 180 - -/38/ - 0.51 ≤ t < 4.762 0.020 ≤ t < 0.1875 1035 150 1240 180 - -/38/ -

Pl, Sh, St/

PHT:

1400+55+1050

4.762 ≤ t < 15.88 0.1875 ≤ t < 0.625 965 140 1170 170 20 -/38/ - 0.038 ≤ t < 0.127 0.0015 ≤ t < 0.0050 1310 190 1450 210 - -/44/ - 0.127 ≤ t < 0.25 0.0050 ≤ t < 0.0010 1310 190 1450 210 - -/44/ - 0.25 ≤ t < 0.51 0.010 ≤ t < 0.020 1310 190 1450 210 - -/44/ - 0.51 ≤ t < 4.762 0.020 ≤ t < 0.1875 1310 190 1450 210 - -/44/ -

Trang 3

or MPa ksi N/mm

2 or MPa ksi

Pl, Sh, St/

S 0.038 ≤ t < 102 0.0015≤ t < 4.0 450 65 1035 150 25 -/100HRB/ -

0.038 ≤ t < 0.127 0.0015 ≤ t < 0.0050 1170 170 1310 190 - -/40/ - 0.127 ≤ t < 0.25 0.0050 ≤ t < 0.0010 1170 170 1310 190 - -/40/ - 0.25 ≤ t < 0.51 0.010 ≤ t < 0.020 1170 170 1310 190 - -/40/ - 0.51 ≤ t < 4.762 0.020 ≤ t < 0.1875 1170 170 1310 190 - -/40/ -

Pl, Sh, St/

1400+55+1050

4.762 ≤ t < 15.88 0.1875 ≤ t < 0.625 1170 170 1310 190 20 375/40/ - 0.038 ≤ t < 0.127 0.0015 ≤ t < 0.0050 1380 200 1550 225 - -/46/ - 0.127 ≤ t < 0.25 0.0050 ≤ t < 0.0010 1380 200 1550 225 - -/46/ - 0.25 ≤ t < 0.51 0.010 ≤ t < 0.020 1380 200 1550 225 - -/46/ - 0.51 ≤ t < 4.762 0.020 ≤ t < 0.1875 1380 200 1550 225 - -/46/ -

Pl, Sh, St/

1750+minus 100+950

4.762 ≤ t < 15.88 0.1875 ≤ t < 0.625 1380 200 1550 225 20 429/45/ -

Pl, Sh, St/

CR 0.038 ≤ t < 0.13 0.0015 ≤ t < 0.0050 1205 175 1380 200 - -/41/ - ASTM A 693-03 632 - S15700

Pl, Sh, St/

CR+900 0.038 ≤ t < 0.13 0.0015 ≤ t < 0.0050 1585 230 1655 240 - -/46/ - St/

EN 10088-2:1995 X8CrNiMoAl15-7-2 1.4532 -

St/

Trang 4

8.1.5A Chemical Composition of Duplex (Ferritic-Austenitic) Stainless Steels

Weight, %, max, Unless Otherwise Specified Standard

Designation

Grade, Class, Type, Symbol or Name

Steel Number

EN 10088-2:1995 X2CrNiMoCuN25-6-3 1.4507 - 0.030 2.00 0.70 0.035 0.015 24.00-26.00 5.50-7.50 2.70-4.00 N 0.15-0.30; Cu 1.00-2.50 ASTM A 240/A 240M-03c 2507 - S32750 0.030 1.20 0.80 0.035 0.020 24.0-26.0 6.0-8.0 3.0-5.0 N 0.24-0.32; Cu 0.50

EN 10088-2:1995 X2CrNiMoN25-7-4 1.4410 - 0.030 2.00 1.00 0.035 0.015 24.00-26.00 6.00-8.00 3.00-4.50 N 0.20-0.35

ASTM A 240/A 240M-03c - - S32760 0.030 1.00 1.00 0.030 0.010 24.0-26.0 6.0-8.0 3.0-4.0 N 0.20-0.30; Cu 0.50-1.00; W 0.50-1.00

EN 10088-2:1995 X2CrNiMoCuWN25-7-4 1.4501 - 0.030 1.00 1.00 0.035 0.015 24.00-26.00 6.00-8.00 3.00-4.00 N 0.20-0.30; Cu 0.50-1.00; W 0.50-1.00

Trang 5

8.1.5B Mechanical Properties of Duplex (Ferritic-Austenitic) Stainless Steels

Designation Grade, Class, Type, Symbol or Name Number Steel Number UNS Heat Treatment Product Form/ t, mm t, in N/mm 2 or

2 or

Elongation, min, % Hardness, max HB/HRB/HV

ASTM A 240/A 240M-03c 2205 - S32205 Pl, Sh, St - - 450 65 655 95 25 293/31/ - JIS G 4304:1999 SUS329J3L - - Pl, Sh, St/HR, S - - 450 - 620 - 18 302/32/320

Trang 6

8.2.1A Chemical Composition of Martensitic Stainless Steels

Designation

Grade, Class, Type, Symbol

ASTM A 582/A 582M-95b (2000) 416 - S41600 0.15 1.25 1.00 0.06 0.15 min 12.00-14.00 - - -

JIS G 4303:1998 SUS416 - - 0.15 1.25 1.00 0.060 0.15 min 12.00-14.00 - 0.60 -

JIS G 4318:1998 SUS416 - - 0.15 1.25 1.00 0.060 0.15 min 12.00-14.00 - 0.60 -

ASTM A 582/A 582M-95b (2000) 420F - S42020 0.30-0.40 1.25 1.00 0.06 0.15 min 12.00-14.00 0.50 - -

JIS G 4303:1998 SUS420F - - 0.26-0.40 1.25 1.00 0.060 0.15 min 12.00-14.00 - 0.60 -

JIS G 4318:1998 SUS420F - - 0.26-0.40 1.25 1.00 0.060 0.15 min 12.00-14.00 - 0.60 -

Trang 7

8.2.1A Chemical Composition of Martensitic Stainless Steels (Continued)

Designation

Trang 8

8.2.1B Mechanical Properties of Martensitic Stainless Steels

Designation

or Name

Steel Number Number UNS Heat Treatment Product Form/ t, mm t, in N/mm 2 or

2 or

JIS G 4318:1998 SUS403 - - Bar/CF mechanical properties of bars shall be agreed upon between the parties concerned with delivery

Bar/HF or CF, A - - - - 730 max - - 220/ -/ -

EN 10088-3:1995 X12Cr13 1.4006 - Bar/

HF or CF, QT650 ≤ 160 - 450 - 650-850 - 15 -/ -/ - Bar/HF or CF, A - - - - - - - 262/ -/ - Bar/HF or CF, T - - - - - - - 248-302/ -/ - ASTM A 582/A 582M-95b (2000) 416 - S41600

Bar/HF or CF, H - - - - - - - 293-352/ -/ -

Bar/HF or CF, A - - - - 730 max - - 220/ -/ -

EN 10088-3:1995 X12CrS13 1.4005 - Bar/

HF or CF, QT650 ≤ 160 - 450 - 650-850 - 12 -/ -/ - JIS G 4303:1998 SUS420J1 - - Bar/HF, Q ≤ 75 - 440 - 640 - 20 192 min/ -/ - JIS G 4318:1998 SUS420J1 - - Bar/CF mechanical properties of bars shall be agreed upon between the parties concerned with delivery

Bar/HF or CF, A - - - - 760 max - - 230/ -/ - Bar/HF or CF, T700 ≤ 160 - 500 - 700-850 - 13 -/ -/ -

EN 10088-3:1995 X20Cr13 1.4021 -

Bar/HF or CF, T800 ≤ 160 - 600 - 800-950 - 12 -/ -/ - JIS G 4303:1998 SUS420J2 - - Bar/HF, Q ≤ 75 - 540 - 740 - 12 217 min/ -/ - JIS G 4318:1998 SUS420J2 - - Bar/CF mechanical properties of bars shall be agreed upon between the parties concerned with delivery

Bar/HF or CF, A - - - - 800 max - - 245/ -/ -

EN 10088-3:1995 X30Cr13 1.4028 -

Bar/HF or CF, T850 ≤ 160 - 650 - 850-1000 - 10 -/ -/ -

Trang 9

8.2.1B Mechanical Properties of Martensitic Stainless Steels (Continued)

Designation

or Name

2 or

ASTM A 582/A 582M-95b (2000) 420F - S42020 Bar/HF or CF, A - - - - - - - 262/ -/ -

JIS G 4303:1998 SUS420F - - Bar/HF, Q ≤ 75 - 540 - 740 - 8 217 min/ -/ -

JIS G 4318:1998 SUS420F - - Bar/CF mechanical properties of bars shall be agreed upon between the parties concerned with delivery

Bar/HF or CF, A - - - - 800 max - - 245/ -/ -

EN 10088-3:1995 X29CrS13 1.4029 -

Bar/HF or CF, T850 ≤ 160 - 650 - 850-1000 - 9 -/ -/ - ASTM A 276-03 431 - S43100 Bar, Shape/

Bar, Shape/CF, A all all - - - - - 285/ -/ - JIS G 4303:1998 SUS440A - - Bar/HF, Q ≤ 75 - - - - - - -/54 min/ -

EN 10088-3:1995 X70CrMo15 1.4109 - Bar/HF or CF, A ≤ 100 - - - 900 max - - 280/ -/ -

Bar, Shape/HF, A all all - - - - - 269/ -/ - ASTM A 276-03 440B - S44003

Bar, Shape/CF, A all all - - - - - 285/ -/ - JIS G 4303:1998 SUS440B - - Bar/HF, Q ≤ 75 - - - - - - -/56 min/ -

Bar, Shape/HF, A all all - - - - - 269/ -/ - ASTM A 276-03 440C - S44004

Bar, Shape/CF, A all all - - - - - 285/ -/ - JIS G 4303:1998 SUS440C - - Bar/HF, Q ≤ 75 - - - - - - -/58 min/ -

JIS G 4318:1998 SUS440C - - Bar/CF mechanical properties of bars shall be agreed upon between the parties concerned with delivery

EN 10088-3:1995 X105CrMo17 1.4125 - Bar/HF or CF, A ≤ 100 - - - - - - 285/ -/ -

Trang 10

8.2.2A Chemical Composition of Ferritic Stainless Steels

Designation

ASTM A 582/A 582M-95b (2000) 430F - S43020 0.12 1.25 1.00 0.060 0.15 min 16.00-18.00 - - -

JIS G 4303:1998 SUS430F - - 0.12 1.25 1.00 0.060 0.15 min 16.00-18.00 - - -

JIS G 4318:1998 SUS430F - - 0.12 1.25 1.00 0.060 0.15 min 16.00-18.00 - - -

EN 10088-3:1995 X6CrMoS17 1.4105 - 0.08 1.50 1.50 0.040 0.15-0.35 16.00-18.00 - 0.20-0.60 -

ISO 4955:1994 X6Cr17 - - 0.08 1.0 1.0 0.040 0.030 16.0-18.0 1.0 - -

ASTM A 582/A 582M-95b (2000) - - S18235 0.025 0.50 1.00 0.030 0.15-0.35 17.05-18.50 1.00 2.00-2.50 N 0.025; Ti 0.30-1.00; C+N 0.035

EN 10088-3:1995 X2CrMoTiS18-2 1.4523 - 0.030 0.50 1.00 0.040 0.15-0.35 17.50-19.00 - 2.00-2.50 C+N 0.040 JIS G 4303:1998 SUS434 - - 0.12 1.00 1.00 0.040 0.030 16.00-18.00 - 0.75-1.25 -

EN 10088-3:1995 X6CrMo17-1 1.4113 - 0.08 1.00 1.00 0.040 0.030 16.00-18.00 - 0.90-1.40 -

ASTM A 276-03 447 - S44700 0.010 0.30 0.20 0.025 0.020 28.0-30.0 0.15 3.5-4.2 N 0.020; Cu 0.15; C+N 0.025 JIS G 4303:1998 SUS447J1 - - 0.010 0.40 0.40 0.030 0.020 28.50-32.00 0.50 1.50-2.50 N 0.015; Cu 0.20; Ni+Cu 0.50 ASTM A 276-03 XM-27 - S44627 0.010 0.40 0.40 0.020 0.020 25.0-27.5 0.50 0.75-1.50 N 0.015; Cu 0.20; Cb 0.05-0.20 JIS G 4303:1998 SUSXM27 - - 0.010 0.40 0.40 0.030 0.020 25.00-27.50 0.50 0.75-1.50 N 0.015; Cu 0.20; Ni+Cu 0.50 ASTM A 276-03 446 - S44600 0.20 1.50 1.00 0.040 0.030 23.0-27.0 0.75 - N 0.25

JIS G 4311:1991 SUH446 - - 0.20 1.50 1.00 0.040 0.030 23.00-27.00 - - N 0.25

ISO 4955:1994 X15CrN26 - - 0.20 1.0 1.0 0.040 0.030 24.0-28.0 1.0 - N 0.15-0.25

EN 10095:1999 X18CrN28 1.4749 - 0.15-0.20 1.00 1.00 0.040 0.015 26.00-29.00 - - N 0.15-0.25

Trang 11

8.2.2B Mechanical Properties of Ferritic Stainless Steels

Designation

or Name

2 or

Elongation, min, %

Hardness, max HB/HRB/HV

Bar, Shape/HF, A all all - - - - - 207/ -/ - ASTM A 276-03 405 - S40500

Bar, Shape/CF, A all all - - - - - 217/ -/ -

EN 10088-3:1995 X6Cr13 1.4000 - Bar/HF or CF, A ≤ 25 - 230 - 400-630 - 20 200/ -/ - ISO 4955:1994 X6Cr13 - - Bar/TA - - 230 - 400-630 - see standard 197/ -/ -

ASTM A 276-03 430 - S43000 Bar, Shape/

EN 10088-3:1995 X6Cr17 1.4016 - Bar/HF or CF, A ≤ 100 - 240 - 400-630 - 20 200/ -/ - ASTM A 582/A 582M-95b (2000) 430F - S43020 Bar/HF or CF, A - - - - - - - 262/ -/ -

JIS G 4318:1998 SUS430F - - Bar/CF mechanical properties of bars shall be agreed upon between the parties concerned with delivery

EN 10088-3:1995 X6CrMoS17 1.4105 - Bar/HF or CF, A ≤ 100 - 250 - 430-630 - 20 200/ -/ - ISO 4955:1994 X6Cr17 - - Pl, Sh, St/TA 5 < t ≤ 15 - 250 - 430-630 - see standard 197/ -/ -

ASTM A 582/A 582M-95b (2000) - - S18235 Bar/HF or CF, A - - - - - - - 207/ -/ -

Bar, Shape/CF, A all all 415 60 520 75 15 -/ -/ -

Bar, Shape/HF, A all all 275 40 450 65 20 219/ -/ - ASTM A 276-03 XM-27 - S44627

Bar, Shape/CF, A all all 275 40 450 65 16 219/ -/ -

Bar, Shape/HF, A all all 275 40 450 65 20 219/ -/ - ASTM A 276-03 446 - S44600

Bar, Shape/CF, A all all 275 40 450 65 16 219/ -/ - JIS G 4311:1991 SUH446 - - Bar/HF, A - - 275 - 510 - 20 201/ -/ -

ISO 4955:1994 X15CrN26 - - Bar/TA - - 280 - 500-700 - see standard 212/ -/ -

EN 10095:1999 X18CrN28 1.4749 - Rod, Section/ A ≤ 25 - 280 - 500-700 - see standard 212/ -/ -

Trang 12

8.2.3A Chemical Composition of Austenitic Stainless Steels

Designation

JIS G 4303:1998 SUS302 - - 0.15 2.00 0.75 0.045 0.030 17.00-19.00 8.00-10.00 - -

JIS G 4318:1998 SUS302 - - 0.15 2.00 0.75 0.045 0.030 17.00-19.00 8.00-10.00 - -

ASTM A 582/A 582M-95b (2000) 303 - S30300 0.15 2.00 1.00 0.20 0.15 min 17.00-19.00 8.00-10.00 - -

JIS G 4303:1998 SUS303 - - 0.15 2.00 1.00 0.20 0.15 min 17.00-19.00 8.00-10.00 0.60 -

JIS G 4318:1998 SUS303 - - 0.15 2.00 1.00 0.20 0.15 min 17.00-19.00 8.00-10.00 0.60 -

EN 10088-3:1995 X8CrNiS18-9 1.4305 - 0.10 2.00 1.00 0.045 0.15-0.35 17.00-19.00 8.00-10.00 - N 0.11; Cu 1.00

ASTM A 582/A 582M-95b (2000) 303Se - S30323 0.15 2.00 1.00 0.20 0.06 17.00-19.00 8.00-10.00 - Se 0.15 min

JIS G 4303:1998 SUS303Se - - 0.15 2.00 1.00 0.20 0.06 17.00-19.00 8.00-10.00 0.60 Se 0.15 min

JIS G 4318:1998 SUS303Se - - 0.15 2.00 1.00 0.20 0.06 17.00-19.00 8.00-10.00 0.60 Se 0.15 min

JIS G 4303:1998 SUS304N1 - - 0.08 2.50 1.00 0.045 0.030 18.00-20.00 7.00-10.50 - N 0.10-0.25

ASTM A 276-03 304LN - S30453 0.030 2.00 1.00 0.045 0.030 18.0-20.0 8.0-11.0 - N 0.10-0.16

JIS G 4303:1998 SUS304LN - - 0.030 2.00 1.00 0.045 0.030 17.00-19.00 8.50-11.50 - N 0.12-0.22

EN 10088-3:1995 X2CrNiN18-10 1.4311 - 0.030 2.00 1.00 0.045 0.030 17.00-19.50 8.50-11.50 - N 0.12-0.22 ASTM A 276-03 XM-21 - S30452 0.08 2.00 1.00 0.045 0.030 18.0-20.0 8.0-10.0 - N 0.16-0.30

JIS G 4303:1998 SUS304N2 - - 0.08 2.50 1.00 0.045 0.030 18.00-20.00 7.50-10.50 - N 0.15-0.30; Nb 0.15

Trang 13

8.2.3A Chemical Composition of Austenitic Stainless Steels (Continued)

Designation

Steel Number

JIS G 4303:1998 SUS316L - - 0.030 2.00 1.00 0.045 0.030 16.00-18.00 12.00-15.00 2.00-3.00 -

JIS G 4318:1998 SUS316L - - 0.030 2.00 1.00 0.045 0.030 16.00-18.00 12.00-15.00 2.00-3.00 -

X2CrNiMo17-12-2 1.4404 - 0.030 2.00 1.00 0.045 0.030 16.50-18.50 10.00-13.00 2.00-2.50 N 0.11 X2CrNiMo17-12-3 1.4432 - 0.030 2.00 1.00 0.045 0.030 16.50-18.50 10.50-13.00 2.50-3.00 N 0.11

EN 10088-3:1995

X2CrNiMo18-14-3 1.4435 - 0.030 2.00 1.00 0.045 0.030 17.00-19.00 12.50-15.00 2.50-3.00 N 0.11 ASTM A 276-03 316N - S31651 0.08 2.00 1.00 0.045 0.030 16.0-18.0 10.0-14.0 2.00-3.00 N 0.10-0.16

Trang 14

8.2.3A Chemical Composition of Austenitic Stainless Steels (Continued)

Designation

Steel Number

UNS

ASTM A 276-03 316Ti - S31635 0.08 2.00 1.00 0.045 0.030 16.0-18.0 10.0-14.0 2.00-3.00 N 0.10; Ti 5 x(C+N) to 0.70 JIS G 4303:1998 SUS316Ti - - 0.08 2.00 1.00 0.045 0.030 16.00-18.00 10.00-14.00 2.00-3.00 Ti 5 x C min

JIS G 4311:1991 SUS316Ti - - 0.08 2.00 1.00 0.045 0.030 16.00-18.00 10.00-14.00 2.00-3.00 Ti 5 x C min

EN 10088-3:1995 X2CrNiMoN17-13-5 1.4439 - 0.030 2.00 1.00 0.045 0.015 16.50-18.50 12.50-14.50 4.00-5.00 N 0.12-0.22 ASTM B 691-02 - - N08367 0.030 2.00 1.00 0.040 0.030 20.00-22.00 23.50-25.50 6.00-7.00 N 0.18-0.25; Cu 0.75 JIS G 4303:1998 SUS836L - - 0.030 2.00 1.00 0.045 0.030 19.00-24.00 24.00-26.00 5.00-7.00 N 0.25

ASTM B 649-02 - - N08904 0.020 2.00 1.00 0.045 0.035 19.00-23.00 23.00-28.00 4.00-5.00 Cu 1.0-2.0

JIS G 4303:1998 SUS890L - - 0.020 2.00 1.00 0.045 0.030 19.00-23.00 23.00-28.00 4.00-5.00 Cu 1.00-2.00

EN 10088-3:1995 X1NiCrMoCu25-20-5 1.4539 - 0.020 2.00 0.70 0.030 0.010 19.00-21.00 24.00-26.00 4.00-5.00 N 0.15; Cu 1.20-2.00 ASTM A 276-03 321 - S32100 0.08 2.00 1.00 0.045 0.030 17.0-19.0 9.0-12.0 - Ti 5 x (C+N) to 0.70 JIS G 4303:1998 SUS321 - - 0.08 2.00 1.00 0.045 0.030 17.00-19.00 9.00-13.00 - Ti 5 x C min

JIS G 4318:1998 SUS321 - - 0.08 2.00 1.00 0.045 0.030 17.00-19.00 9.00-13.00 - Ti 5 x C min

JIS G 4311:1991 SUS321 - - 0.08 2.00 1.00 0.045 0.030 17.00-19.00 9.00-13.00 - Ti 5 x C min

EN 10088-3:1995 X6CrNiTi18-10 1.4541 - 0.08 2.00 1.00 0.045 0.030 17.00-19.00 9.00-12.00 - Ti 5 x C to 0.70

ISO 4955:1994 X7CrNiTi18-10 - - 0.040-0.10 2.0 1.0 0.045 0.030 17.0-19.0 9.0-12.0 - Ti 5 x C to 0.80

ASTM A 276-03 347 - S34700 0.08 2.00 1.00 0.045 0.030 17.0-19.0 9.0-12.0 - Cb 10 x C to 1.10 JIS G 4303:1998 SUS347 - - 0.08 2.00 1.00 0.045 0.030 17.00-19.00 9.00-13.00 - Nb 10 x C min

JIS G 4311:1991 SUS347 - - 0.08 2.00 1.00 0.045 0.030 17.00-19.00 9.00-13.00 - Nb 10 x C min

JIS G 4318:1998 SUS347 - - 0.08 2.00 1.00 0.045 0.030 17.00-19.00 9.00-13.00 - Nb 10 x C min

EN 10088-3:1995 X6CrNiNb18-10 1.4550 - 0.08 2.00 1.00 0.045 0.015 17.00-19.00 9.00-12.00 - Nb 10 x C to 1.00 ISO 4955:1994 X7CrNiNb18-10 - - 0.040-0.10 2.0 1.0 0.045 0.030 17.0-19.0 9.0-12.0 - Nb 10 x C to 1.2

Trang 15

8.2.3B Mechanical Properties of Austenitic Stainless Steels

Designation

or Name

2 or

ASTM A 276-03 201 - S20100 Bar, Shape/

ASTM A 276-03 202 - S20200

Bar, Shape/

CF, B

38.10 < t ≤ 44.45 1½ < t ≤ 1¾ 310 45 655 95 28 -/ -/ -

ASTM A 276-03 302 - S30200

Bar, Shape/CF, B

38.10 < t ≤ 44.45 1½ < t ≤ 1¾ 310 45 655 95 28 -/ -/ -

ASTM A 582/A 582M-95b (2000) 303 - S30300 Bar/HF or CF, A - - - - - - - 262/ -/ -

EN 10088-3:1995 X8CrNiS18-9 1.4305 - Bar/HF or CF, AT ≤ 160 - 190 - 500-750 - 35 230/ -/ - ASTM A 582/A 582M-95b (2000) 303Se - S30323 Bar/HF or CF, A - - - - - - - 262/ -/ -

JIS G 4318:1998 SUS303Se - - Bar/CF mechanical properties of bars shall be agreed upon between the parties concerned with delivery

Trang 16

8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued)

Designation

or Name

2 or

Bar, Shape/HF, A all all 205 30 515 75 40 -/ -/ -

EN 10088-3:1995 X5CrNi18-10 1.4301 - Bar/HF or CF, AT

160 < t ≤ 250 - 190 - 500-700 - T: 35 215/ -/ - Bar, Shape/HF, A all all 170 25 485 70 40 -/ -/ -

ASTM A 276-03 304L - S30403

Bar, Shape/CF, A

> 12.70 > ½ 170 25 485 70 30 -/ -/ -

JIS G 4318:1998 SUS304L - - Bar/CF mechanical properties of bars shall be agreed upon between the parties concerned with delivery

160 < t ≤ 250 - 175 - 450-680 - T: 35 215/ -/ - Bar, Shape/

19.05 < t ≤ 25.40 ¾ < t ≤ 1 550 80 795 115 15 -/ -/ - 25.40 < t ≤ 31.75 1 < t ≤ 1¼ 450 65 725 105 20 -/ -/ - 31.75 < t ≤ 38.10 1¼ < t ≤ 1½ 345 50 690 100 24 -/ -/ - Bar, Shape/CF, B

Trang 17

Designation

or Name

2 or

ASTM A 276-03 305 - S30500

Bar, Shape/CF, A

> 12.70 > ½ 205 30 515 75 30 -/ -/ -

ASTM A 276-03 309S - S30908

Bar, Shape/CF,A

> 12.70 > ½ 205 30 515 75 30 -/ -/ -

JIS G 4318:1998 SUS309S - - Bar/CF mechanical properties of bars shall be agreed upon between the parties concerned with delivery

ISO 4955:1994 X6CrNi23-14 - - Bar/TQ - - 210 - 500-700 - see standard 192/ -/ -

ASTM A 276-03 310S - S31008

Bar, Shape/CF, A

> 12.70 > ½ 205 30 515 75 30 -/ -/ -

JIS G 4318:1998 SUS310S - - Bar/CF mechanical properties of bars shall be agreed upon between the parties concerned with delivery

ISO 4955:1994 X6CrNi25-21 - - Pl, Sh, St/TQ ≤ 100 - 210 - 500-700 - see standard 192/ -/ -

Trang 18

Designation

2 or

ASTM A 276-03 316L - S31603

Bar, Shape/CF, A

> 12.70 > ½ 170 25 485 70 30 -/ -/ -

JIS G 4318:1998 SUS316L - - Bar/CF mechanical properties of bars shall be agreed upon between the parties concerned with delivery

Trang 19

2 or

Bar, Shape/

19.05 < t ≤ 25.40 ¾ < t ≤ 1 550 80 795 115 15 -/ -/ - 25.40 < t ≤ 31.75 1 < t ≤ 1¼ 450 65 725 105 20 -/ -/ - 31.75 < t ≤ 38.10 1¼ < t ≤ 1½ 345 50 690 100 24 -/ -/ - Bar, Shape/CF, B

ASTM A 276-03 316Ti - S31635

Bar, Shape/CF, A

> 12.70 > ½ 205 30 515 75 30 -/ -/ -

EN 10088-3:1995 X6CrNiMoTi17-12-2 1.4571 - Bar/HF or CF, AT

ASTM A 276-03 317 - S31700

Bar, Shape/CF, A

> 12.70 > ½ 205 30 515 75 30 -/ -/ -

Trang 20

2 or

EN 10088-3:1995 X2CrNiMoN17-13-5 1.4439 - Bar/HF or CF, AT

160 < t ≤ 250 - 280 - 580-800 - T: 30 250/ -/ - ASTM B 691-02 - - N08367 Bar/HF or CF, A all all 310 45 655 95 30 -/ -/ -

ASTM B 649-02 - - N08904 Bar/HF or CF, ST all all 220 31 490 71 35 -/ -/ -

EN 10088-3:1995 X1NiCrMoCu25-20-5 1.4539 - Bar/HF or CF, AT

ASTM A 276-03 321 - S32100

Bar, Shape/CF, A

> 12.70 > ½ 205 30 515 75 30 -/ -/ -

EN 10088-3:1995 X6CrNiTi18-10 1.4541 - Bar/HF or CF, AT

160 < t ≤ 250 - 190 - 500-700 - T: 30 215/ -/ - ISO 4955:1994 X7CrNiTi18-10 - - Bar/TQ - - 200 - 510-710 - see standard 192/ -/ -

ASTM A 276-03 347 - S34700

Bar, Shape/CF, A

> 12.70 > ½ 205 30 515 75 30 -/ -/ -

EN 10088-3:1995 X6CrNiNb18-10 1.4550 - Bar/HF or CF, AT

160 < t ≤ 250 - 205 - 510-740 - T: 30 230/ -/ - ISO 4955:1994 X7CrNiNb18-10 - - Bar/TQ - - 205 - 510-710 - see standard 192/ -/ -

ASTM A 276-03 309 - S30900

Bar, Shape/CF, A

> 12.70 > ½ 205 30 515 75 30 -/ -/ -

EN 10095:1999 X12CrNi23-13 1.4833 - Bar/HF or CF, AT - - 210 - 500-700 - see standard 192/ -/ -

ASTM A 276-03 310 - S31000

Bar, Shape/CF, A

> 12.70 > ½ 205 30 515 75 30 -/ -/ -

EN 10095:1999 X15CrNiSi25-21 1.4841 - Bar/HF or CF, AT - - 230 - 550-750 - see standard 223/ -/ -

ISO 4955:1994 X15CrNiSi25-21 - - Bar/TQ - - 230 - 550-750 - see standard 223/ -/ -

Tiêu đề	Mechanical Properties of Precipitation-Hardening Stainless Steels
Trường học	Unknown University
Chuyên ngành	Materials Engineering
Thể loại	Standards Document
Năm xuất bản	1999
Thành phố	Unknown City

Định dạng
Số trang	40
Dung lượng	272,31 KB