In the present work, C@TiO2 core-shell adsorbents were successfully prepared and the adsorption capacities for rhodamine B (RB) were investigated at different conditions. The adsorbents were prepared by first in-situ hydrolysis and deposition of TBOT on the surface of ZIF-8 nanoparticles to obtain ZIF-8@titania gel, and then carbonization.
Trang 1Available online 16 April 2021
1387-1811/© 2021 The Authors Published by Elsevier Inc This is an open access article under the CC BY-NC-ND license ( http://creativecommons.org/licenses/by-nc-nd/4.0/ ).
aqueous solution
Kang Lia, Liang Yub,*, Juanjuan Caia, Lixiong Zhanga,**
aState Key Laboratory of Materials-Oriented Chemical Engineering, College of Chemistry and Chemical Engineering, Nanjing Tech University, Nanjing, 211816, China
bChemical Technology, Luleå University of Technology, SE-971 87, Luleå, Sweden
A R T I C L E I N F O
Keywords:
ZIF-8
Titania
C@TiO 2 adsorbents
Rhodamine B
Wastewater treatment
A B S T R A C T
In the present work, C@TiO2 core-shell adsorbents were successfully prepared and the adsorption capacities for rhodamine B (RB) were investigated at different conditions The adsorbents were prepared by first in-situ hy-drolysis and deposition of TBOT on the surface of ZIF-8 nanoparticles to obtain ZIF-8@titania gel, and then carbonization XRD, SEM, TEM, and N2 adsorption-desorption techniques were employed to characterize the adsorbents The results showed that the adsorbents were comprised of TiO2 shell and carbon core Large surface area and hierarchical pores, which were different from ZIF-8 derived porous carbon, were generated due to the less contraction of carbon during carbonization when robust TiO2 shell covered on the surface The highest adsorption capacity for RB was 298 mg/g on C@TiO2 Apart from the hierarchical pores and large surface area, the low surface charge of C@TiO2 core-shell adsorbents was also observed, which also contributed to the high adsorption capacity for cationic dyes The reuse experiments showed that the adsorbents maintained the high adsorption capacity after 5 cycles The high stability is crucial for practical application
1 Introduction
Adsorption, as an efficient process for wastewater treatment, has
drawn much research attention Therefore, the development of high
performance and cost-effective adsorbents for the removal of organic
contaminants like dyes from textile dyeing effluents are of a great
in-terest [1–3] Porous carbons have been considered as efficient
adsor-bents for various adsorption applications due to the porous structure,
high stability and environmentally friendly properties However,
microporous biochar [4] and activated carbon [5] displayed low
adsorption capacities of 86 and 55 mg/g, respectively, for RB The low
adsorption capacity resulted from the small pore size Higher adsorption
capacities of 284 and 423 mg/g were observed for brilliant yellow and
RB on mesoporous carbons due to the larger pore size and pore volume
[6] Graphene-like porous carbon with even higher surface area (1710
m2/g) and pore volume (0.83 cm3/g) showed excellent adsorption
ca-pacity of 418 mg/g for methyl orange [7] However, for many carbon
materials, the preparation procedures were complicated and the
im-provements of pore systems and surface chemistry are needed from
higher adsorption performance
Many methods have been developed to prepare carbons with unique structures [8] and surface chemistry for higher adsorption capacity [9] Carbon composites combined the advantage of at least two materials, which could display significantly higher adsorption capacity than the single component materials For instance, porous carbon nanosheets (PCNSs) comprised of two different carbons sources were prepared by carbonizing of waste plastics covered organically-modified montmoril-lonite The surface area (2315 m2/g) and pore volume (3.3 cm3/g) of the carbon materials were large, and the surface zeta potential was low Therefore, the adsorption capacity for methylene blue was unprece-dentedly high about 769 mg/g [10] For RB adsorption, an adsorption capacity of 625 mg/g on montmorillonite/graphene oxide nano-composites was observed, which was higher than that of montmoril-lonite and graphene oxide [11] The synergistic effect of the components
in the nanocomposites contributed to the high adsorption capacity [11]
In addition, composites could generate hierarchically structured porous materials, which can improve the mass transfer efficiently
Our group also developed several composites that showed high performance for gas upgrading and wastewater treatment For example, NaX/NaA core-shell microspheres showed a higher adsorption
* Corresponding author
** Corresponding author
Contents lists available at ScienceDirect Microporous and Mesoporous Materials journal homepage: http://www.elsevier.com/locate/micromeso
https://doi.org/10.1016/j.micromeso.2021.111110
Received 15 February 2021; Received in revised form 20 March 2021; Accepted 13 April 2021
Trang 2selectivity for CO2/N2 compared to NaX microspheres [12] Hollow
zeolite NaA/chitosan composite microspheres prepared in a simple
microchannel device showed an adsorption capacity of 16 mg/g for
Cu2+from water at the studied conditions [13] Carbon/cobalt
com-posites were simply prepared by carbonization the mixtures of phenolic
resin and ZIF-67 The composites displayed high adsorption capacity of
2778 mg/g for tannic acid In contrast, the adsorption capacity was 205
and 1375 mg/g on phenolic resin and ZIF-67 derived carbons,
respec-tively [14] Core-shell composites prepared by coating one component
on the surface of the other can exhibit different properties for different
applications due to the change of the surface chemistry [15] Recently,
we reported a C@silica core-shell adsorbent for the adsorption of
cip-rofloxacin [16] ZIF-8 was used as the carbon source Moreover, ZIF-8 is
a microporous metal-organic framework material composing of Zn
cat-ions coordinated to 2-methyimodazole linkers The observed adsorption
capacity was1575 mg/g at the optimum adsorption conditions Besides,
the results also showed that the charge on the core-shell nanoparticles
was more negatively due to the effect of silica shell, thereby improving
the adsorption capacity Very recently, we also reported a porous C@C
composite adsorbent for the adsorption of dye contaminants from water
The adsorbents were prepared from the carbonization of
resorci-nol–formaldehyde (RF) resins@ZIF-8 composites [17] The surface area
of the C@C composite adsorbent was much higher than the single
components derived carbons Meanwhile, the pore size of the C@C
composite adsorbent was slightly larger Therefore, the adsorption
ca-pacities of the composite adsorbents for methylene blue and RB was as
high as 681 and 462 mg/g, respectively Interestingly, the results also
showed a lower surface charge on composite, which also enhanced the
adsorption All the developed composites displayed high stability and
could be recycled easily, meanwhile, maintained high adsorption
ca-pacity In addition, the results also indicated that surface modification is
an efficient method for the preparation of high performance adsorbents
In the present work, we prepared C@TiO2 core-shell adsorbents by
carbonizing ZIF-8@titania gel core-shell composites The titania gel
coated on the surface ZIF-8 particles by hydrolysing and depositing
TBOT To optimize the preparation conditions, different ratios of TBOT
to ZIF-8 and carbonization temperatures were investigated The effect of
TiO2 shell on the pores and surface chemistry of ZIF-8 derived porous
carbon were explored The obtained composites were used for RB
adsorption and the adsorption conditions were optimized Meanwhile,
the adsorption mechanism was discussed
2.2 Preparation of TiO 2 coated carbon nanoparticles
The obtained ZIF-8 (0.1g) was dispersed in 40 ml ethanol and added 0.062 g tetrabutyl orthotitanate (TBOT) under stirring condition The mass ratio of ZIF-8 and TBOT was 1:0.62 After stirring for 1 h, 70 ml water was added into the solution using a syringe pump The flowrate was 1 ml/min Then, the mixture was stirred for 12 h at room temper-ature The obtained product was recovered by centrifuge The sample was denoted as ZIF-8@titania gel-1 Meanwhile, ZIF-8@titania gel-2 and ZIF-8@titania gel-3 were also prepared using the mass ratio of ZIF-8 and TBOT of 1:1.25 and 1:2.50, respectively
ZIF-8@titania gel-1, ZIF-8@titania gel-2, and ZIF-8@titania gel-3 were carbonized under nitrogen atmosphere to obtain C@TiO2-1, C@TiO2-2, and C@TiO2-3, respectively The carbonization temperature was 700 ◦C and the time was 2 h ZIF-8@titania gel-2 sample was also carbonized at 850 and 1000 ◦C to investigate the effect of carbonization temperature, the obtained products were denoted as C@TiO2-850 and C@TiO2-1000, respectively
2.3 Adsorption experiments
All adsorption experiments were carried out at 30 ◦C and the tem-perature of the solution was controlled by an oil bath C@TiO2 nano-particles (2.5 mg) were added in 50 ml RB aqueous solutions with the concentration of 40 mg/l for adsorption Sodium hydroxide (0.1 M) or hydrogen chloride (0.1 M) aqueous solution was used to adjust the pH The adsorption loading at different adsorption times was determined by analysis of 1 ml solution taken from the bulk solution Prior to analysis, the collected solutions were filtered using 10 μm filter and diluted 10 times RB aqueous solutions with the concentration from 20 to 100 mg/l were used to determine the adsorption isotherms A MAPADA UV-1800
PC spectrophotometer was employed for the determination of RB con-centration at a wavelength of 544 nm
The adsorption loading q for RB was defined as:
q = V
m(C0− C t)
Where V (ml) is RB aqueous solution volume, m (mg) is the mass of C@TiO2 used for adsorption, C0 (mg/l) and Ct (mg/l) are the concen-tration of RB before and after adsorption
2.4 Materials characterizations
Bruker D8 Advance powder X-ray diffractometer (Cu target) was used to record XRD patterns with the tube voltage and current of 40 kV and 40 mA, respectively SEM images was recorded using a field emis-sion scanning electron microscope (Hitachi− S4800) JEOL JEM-2100 transmission electron microscope was employed to recorded TEM im-ages BELSORP II instrument was used to measure the N2 adsorption- desorption isotherms at 77 K The samples were treated at 150 ◦C for
6 h under vacuum before the measurement The BET method was used to calculate the surface area and the total pore volume was estimated at p/
p0 of 0.99
Fig 1 Observed XRD patterns of as-synthesized titania gel, ZIF-8@titania gel-
2, and ZIF-8 Blue bars represent the reference XRD pattern of ZIF-8 (For
interpretation of the references to colour in this figure legend, the reader is
referred to the Web version of this article.)
Trang 33 Results and discussion
3.1 ZIF-8@titania gels particles
As shown in Fig 1, the crystalline structures of the prepared titania
gel, ZIF-8, ZIF-8@titania gel-2 were characterized by XRD The XRD
pattern indicates a high quality ZIF-8 that is confirmed by the simulated
XRD pattern of ZIF-8 as indicated by blue bars [19] No impurity peak
was detected Due to the effect of amorphous titania gel, the peaks
in-tensity of the ZIF-8 became weaker after coating with titania gel
Moreover, the amorphous structure of titania gel resulted from the
ethoxy group (CH3CH2O–) that presented on the surface of the hydro-lysed titania gel and affected the phase change of the gel during drying [20]
SEM images of titania gel, ZIF-8, and ZIF-8@titania gel-2 are given in Fig 2 The SEM image of titania gel shows a structure of agglomerate particles and uneven size The size of the crystals has not changed obviously indicated that a thin titania gel layer covered on ZIF-8 crys-tals Therefore, the morphology of ZIF-8 crystals was preserved in ZIF- 8@titania gel-2 To identify the particle sizes of the obtained samples,
100 particles from each SEM image were measured, and the average particle sizes of 78 ± 17 and 106 ± 20 nm were obtained for ZIF-8
Fig 2 Morphology of titania gel (a), ZIF-8 (b), and ZIF-8@titania gel-2 (c) observed by SEM
Fig 3 XRD patterns (a) and SEM images of ZIF-8@titania gel-1 (b) and ZIF-8@titania gel-3 (c)
Trang 4crystals and ZIF-8@titania gel-2, respectively Therefore, the thickness
of titania gel layer was about 14 nm More details about the structure of
the ZIF-8@titania gel-2 will be discussed below
ZIF-8@titania gel-1 and ZIF-8@titania gel-3 particles prepared from
different mass ratios of ZIF-8 and TBOT were characterized by XRD and
SEM The results are given in Fig 3 The peaks intensity was weaker with
the increase of TBOT due to the thicker titania gel shell on ZIF-8 crystals,
meanwhile, the particles became more agglomerated The average
particle size was about 82 ± 18 nm for ZIF-8@titania gel-1 and 120 ± 21
nm for ZIF-8@titania gel-3, the corresponding titania gel shell thickness
was about 2 and 21 nm, respectively
3.2 C@TiO 2 particles
The XRD patterns of C@TiO2-2, ZIF-8 derived porous carbon and pure TiO2 that were carbonized at 700 ◦C under N2 atmosphere are shown in Fig 4a XRD pattern of the pure TiO2 shows a mixture of anatase and rutile phases This is different from that of the C@TiO2-2, which solely showed a rutile structure It is important to note that ZIF-8 derived porous carbon was an amorphous structure as indicated by XRD pattern Therefore, the differences of phases of TiO2 between pure TiO2
and C@TiO2-2 resulted from the effect of carbon on the phase trans-formation of TiO2 at high temperature It has been reported that the
Fig 4 XRD (a), SEM image of TiO2 (b), C (ZIF-8) (c) and C@TiO2-2 (d) as well as TEM image of C@TiO2-2 (e)
Fig 5 SEM images of C@TiO2-850 (a) and C@TiO2-1000 (b)
Trang 5transformation from anatase to rutile is a reconstructive process In this
process, the chemical bonds will be broken and reformed at high
tem-peratures (>600 ◦C) [21] Apart from temperature, the particle size,
atmosphere, and dopant will also affect the phase transformation As a
strong reducing agent, carbon could enhance the formation of oxygen vacancies in an inert atmosphere thereby promoting the reconstructive process [22] This could explain that almost only rutile was observed in the C@TiO2-2 composite
The morphologies of titania gel and ZIF-8@titania gel-2 were pre-served after high temperature treatment (see Figs 2 and 4) For titania gel, carbonization could be considered as a deep drying process [23] Therefore, the morphology could probably be similar, i.e irregular shape, but smaller size Due to the stable structure of TiO2, the TiO2 shell could maintain the morphology of ZIF-8@titania gel-2 Therefore, the morphology of C@TiO2-2 was similar to ZIF-8@titania gel-2 after high temperature treatment Furthermore, TEM image in Fig 4e clearly shows a core-shell structure of C@TiO2-2 A rational hypothesis is that the core-shell structure comprised of a TiO2 shell with carbon core and the robust TiO2 shell maintained the morphology of ZIF-8@titania gel-2
Fig 6 N2 adsorption-desorption isotherms of samples prepared at different conditions
Table 1
Summary of the textural properties of materials prepared at different conditions
Samples Surface area
(m 2 /g) Total pore volume (cm 3 /g) Average pore size (nm)
C@TiO 2 -
Fig 7 Effect of contact time on the adsorption capacity of ZIF-8 derived
porous carbon, TiO2, C@TiO2-1, C@TiO2-2 and C@TiO2-3 for RB
Fig 8 Adsorption of C@TiO2-2 for RB at different pH (a) and the zeta potential of ZIF-8 derived porous carbon and C@TiO2-2 as a function of pH (b)
Fig 9 Adsorption capacity of C@TiO2 prepared at different carbonization temperatures for RB The precursor of C@TiO2 was ZIF-8@titania gel-2
Trang 6Moreover, the size of C@TiO2-2 was about 92 ± 22 nm and the shell
thickness was about 12 nm The size was slightly smaller than that of
ZIF-8@titania gel-2 due to the contraction during carbonization
Without the support of TiO2 shell, many particles with collapsed
struc-ture were observed in ZIF-8 derived porous carbon (see Fig 4c)
compared to the original ZIF-8 particles (see Fig 2b) The results also
indicated a high stability of C@TiO2-2
SEM images of C@TiO2-850 and C@TiO2-1000 are shown in Fig 5
C@TiO2-850 shows similar morphology to C@TiO2-2 (see Fig 4d)
However, a different structure was observed for C@TiO2-1000, which could be ascribed to the zinc component in the ZIF-8@titania gel The zinc could be evaporated at carbonization temperature due to the low boiling point [24] Therefore, C@TiO2-1000 with a more porous struc-ture was observed
Fig 6 shows N2 adsorption-desorption isotherms of C@TiO2-1, C@TiO2-2, C@TiO2-3, and C@TiO2-1000 as well as TiO2 and ZIF-8 derived porous carbon TiO2 showed the lowest adsorption for N2 due
to the low surface area [25] The steep and high uptake at low relative pressure range (close to zero) indicated that ZIF-8 derived porous carbon has abundant micropores that was similar with that of activated carbons
No hysteresis loop was observed for isotherms of ZIF-8 derived porous carbon that indicates a monomodal pore system Type IV adsorption isotherms were obtained for all core-shell composite adsorbents The adsorption isotherms of C@TiO2 showed high nitrogen adsorption ca-pacity at low pressure range and large hysteresis loop that indicated the materials have abundant micropores and mesopores Meanwhile, the adsorption isotherms of the composites at p/p0 around one increased sharply, which resulted from the macropores Therefore, the results indicated that the synthesized core-shell composites were hierarchically porous materials
The surface area of C (ZIF-8) was 496 m2/g (see Table 1), and it decreased when the TiO2 content increased at the carbonization tem-perature of 700 ◦C However, the surface area was significantly high for sample carbonized at 1000 ◦C due to pores generated during evapora-tion of zinc at high temperature (also see SEM image in Fig 5b) In addition, the total pore volumes and average pore sizes of core-shell adsorbents were much higher than that of C (ZIF-8) due to the support
of TiO2 shell (see SEM images in Fig 4), i.e the robust TiO2 shell moderated the contraction of ZIF-8 derived porous carbon and preserved the pores at high temperature that could benefit the accommodation of large organic dyes molecules Therefore, improved the adsorption
Fig 10 Langmuir (a) and Freundlich (b) linear fitting of adsorption data
Table 2
Different adsorbents for the adsorption of RB from aqueous solution
( ◦ C) Maximum adsorption
capacity (mg/g)
References
Gg-cl-P (AA-co-AAm)/
Bagasse pith derived
Sodium
Humic acid (HA)
modifying Fe 3 O 4
nanoparticles
Treated rice husk-based
solid hazardous waste
scrap tires derived
activated carbon
ZIF-8 derived porous
C@TiO 2 core-shell
Fig 11 Reuse of C@TiO2-1000 for RB adsorption and the morphology of C@TiO2-1000 after 5 times recycling
Trang 73.3 Adsorption of RB
As shown in Fig 7, the maximum loading of RB on the adsorbents C
(ZIF-8 derived), TiO2, C@TiO2-1, C@TiO2-2, C@TiO2-3 were 66, 43,
125, 140 and 105 mg/g, respectively C@TiO2 showed significantly
higher adsorption capacity for RB The adsorption capacities are higher
than that of TiO2 and ZIF-8 derived porous carbon One of the most
important factors for the high adsorption is the larger pore size of the
C@TiO2 composites as shown in Table 1 In addition, the effect of TiO2
on the surface chemistry of carbon could affect the adsorption
To optimize the adsorption capacity, adsorption at different
condi-tions, e.g pH, temperatures, concentrations of RB were investigated
C@TiO2-2 was used as the adsorbent Fig 8a shows that the adsorption
capacity was affected by pH significantly The adsorption loading was
only 29 mg/g at pH of 3 and the loading increased when the pH
increased from 3 to 7 The maximum adsorption loading of 161 mg/g
was observed at pH of 7, and the adsorption loading decreased to 120
mg/g when the pH further increased to 9 The change of the adsorption
loading with pH was ascribed to the different zeta potential of the
adsorbent at different pHs Fig 8b shows that the lower zeta potential of
C@TiO2 composite was observed at higher pH The minimum zeta
po-tential was − 43 mV at pH 7 that would maximize the high adsorption for
cationic RB In addition, zeta potential of the C@TiO2 was lower than
ZIF-8 derived porous carbon due to the presence of TiO2 [26] The zeta
potential of TiO2 decreased dramatically with the increase in the pH has
been reported and a negative charge was obtained when pH higher than
4 [26] Besides, in the pH range of 1–9, the lowest zeta potential of ZIF-8
derived porous carbon was observed at a pH of about 7 [27], which is
similar to the results observed in the present work Therefore, apart from
the effect of robust TiO2 shell on the pores of ZIF-8 derived porous
carbon as discussed above, the ZIF-8 derived porous carbon in
combi-nation with TiO2 could generate an adsorbent with lower zeta potential
Therefore, C@TiO2 core-shell adsorbents showed higher adsorption
performance for cationic dye RB
Our previous work [17] showed that the carbonization temperature
could affect the adsorption capacity of the carbon-based adsorbent The
effect was also investigated in the present work Fig 9 shows the results
when ZIF-8@titania gel-2 was used as the precursor The maximum
adsorption loading was higher for adsorbent prepared at higher
carbonization temperature The adsorption loading was as high as 269
mg/g for C@TiO2 prepared at 1000 ◦C (C@TiO2-1000) that was twofold
of the adsorption loading of C@TiO2 prepared at 700 ◦C As shown in
Table 1, C@TiO2 core-shell adsorbent displayed higher surface area and
pore volume when the carbonization temperature was higher This
could explain the high adsorption capacity of C@TiO2-1000
To explore the adsorption process, the type of adsorption of RB on
C@TiO2 composites was estimated using Langmuir and Freundlich
models The details of these models can be found in the supporting
in-formation C@TiO2-1000 was used as an example due to the highest
adsorption loading as shown above RB aqueous with different
con-centrations was used for the adsorption experiments The adsorption
results can be found in Fig S2a The equilibrium adsorption capacity, i
e the maximum adsorption loading was higher when the RB
concen-tration was higher For instance, the observed maximum adsorption
loading was 258 mg/g for a 20 mg/l RB concentration, and it increased
to 298 mg/g when the RB concentration increased to 100 mg/g Fig 10
shows the Langmuir and Freundlich linear fitting results The adsorption
isotherm is shown in Fig S2b Table S1 summarizes the fitting constants
The results in Fig 10 clearly show that the adsorption isotherms
could be described by Langmuir isotherm model The estimated
maximum adsorption loading was 322 mg/g that was slightly higher
than the experimental results of 298 mg/g The modelling results
indi-cated that the adsorption should be homogeneous monolayer
adsorp-tion This resulted from the electrostatic interaction between cationic RB
molecules and negatively charged surface of adsorbents Table 2
sum-marizes the typical adsorption capacities of different adsorbents for RB
The table shows that our core-shell adsorbents displayed decent adsorption capacity compared to the reported results in the literature
\After adsorption experiment, the C@TiO2-1000 adsorbent was recovered using centrifuge and regenerated by ultrasonic in methanol for 30 min Fig 11a shows that the observed maximum adsorption loading were 269, 278, 257, 262, 258 mg/g, respectively, for 5 consecutive cycles The morphology of the adsorbent was preserved after 5 times reuse that indicated a high stability, see Fig 11b This is important for the real application of the adsorbent
4 Conclusions
C@TiO2 core-shell adsorbents have been successfully prepared by carbonizing ZIF-8@titania gels The adsorbents displayed a hierar-chically porous structure The observed RB adsorption capacity of the core-shell adsorbents was much higher than that of C (ZIF-8) and TiO2 The robust TiO2 shell moderated the contraction of ZIF-8 derived carbon and preserved the pores during carbonization Carbonization tempera-ture and pH of RB aqueous solution are crucial for the adsorption per-formance The surface areas and total pore volumes of the prepared core-shell adsorbents were higher at higher carbonization tempera-ture, which increased the adsorption capacity The adsorbents showed the maximum adsorption loading for RB at pH 7 due the lowest zeta potential A monolayer adsorption state was confirmed by the Langmuir model Due to the robust TiO2 shell, the composite adsorbents showed high stability that makes the materials promising for practical application
CRediT authorship contribution statement Kang Li: Investigation, Formal analysis, Writing – original draft Liang Yu: Conceptualization, Formal analysis, Validation,
Visualiza-tion, Writing – original draft, Writing – review & editing, Resources
Juanjuan Cai: Investigation, Formal analysis Lixiong Zhang:
Conceptualization, Supervision, Writing – review & editing, Funding acquisition
Declaration of competing interest
The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper
Acknowledgements
The Priority Academic Program Development of Jiangsu Higher Education Institutions is acknowledged for financially supporting this work
Appendix A Supplementary data
Supplementary data to this article can be found online at https://doi org/10.1016/j.micromeso.2021.111110
References
[1] S.C Smith, D.F Rodrigues, Carbon 91 (2015) 122–143, https://doi.org/10.1016/j
[2] S De Gisi, G Lofrano, M Grassi, M Notarnicola, SMT Trends 9 (2016) 10–40,
[3] G Crini, E Lichtfouse, L.D Wilson, N Morin-Crini, Environ Chem Lett 17 (2019) 195–213, https://doi.org/10.1007/s10311-018-0786-8
[4] Y Hou, G Huang, J Li, Q Yang, S Huang, J Cai, J Anal Appl Pyrolysis 143 (2019) 104694, https://doi.org/10.1016/j.jaap.2019.104694
[5] M.Z Mohd Nasir, M Abbas Ahmad Zaini, M.A.C Yunus, Desalination Water Treat
132 (2018) 340–349, https://doi.org/10.5004/dwt.2018.23152 [6] X Zhuang, Y Wan, C Feng, Y Shen, D Zhao, Chem Mater 21 (2009) 706–716,
Trang 8287 (2019) 9–17, https://doi.org/10.1016/j.micromeso.2019.05.046
[15] S Wei, Q Wang, J Zhu, L Sun, H Line, Z Guo, Nanoscale 3 (2011) 4474–4502,
[16] Y Li, C Zeng, C Wang, L Zhang, Chem Eng J 342 (2018) 645–653, https://doi
[17] K Li, L Yu, J Cai, L Zhang, Microporous Mesoporous Mater 313 (2021) 110840,
[18] Y Pan, Y Liu, G Zeng, L Zhao, Z Lai, Chem Commun 47 (2011) 2071–2073,
[19] K.S Park, Z Ni, A.P Cote, J.Y Choi, R Huang, F.J Uribe-Romo, H.K Chae,
M O’Keeffe, O.M Yaghi, Proc Natl Acad Sci Unit States Am 103 (2006)
10186–10191, https://doi.org/10.1073/pnas.0602439103
[20] D.C Hague, M.J Mayo, J Am Ceram Soc 77 (1994) 1957–1960, https://doi.org/
[21] D.A.H Hanaor, C.C Sorrell, J Mater Sci 46 (2011) 855–874, https://doi.org/
[22] H Wang, J.P Lewis, J Phys Condens Matter 18 (2006) 421–434, https://doi.org/
[30] T.A Khan, S Dahiya, I Ali, Appl Clay Sci 69 (2012) 58–66, https://doi.org/
[31] H.M.H Gad, A.A El-Sayed, J Hazard Mater 168 (2009) 1070–1081, https://doi
[32] P Panneer Selvam, S Preethi, P Basakaralingam, N Thinakaran, A Sivasamy,
S Sivanesan, J Hazard Mater 155 (2008) 39–44, https://doi.org/10.1016/j
[33] S Wang, Z.H Zhu, J Hazard Mater 136 (2006) 946–952, https://doi.org/
[34] L Peng, P Qin, M Lei, Q Zeng, H Songa, J Yang, J Shao, B Liao, J Gu, J Hazard Mater 209 (2012) 193–198, https://doi.org/10.1016/j.jhazmat.2012.01.011 , 210 [35] J Wang, M Gao, T Shen, M Yu, Y Xiang, J Liu, J Hazard Mater 366 (2019) 501–511, https://doi.org/10.1016/j.jhazmat.2018.12.031
[36] L Ding, B Zou, W Gao, Q Liu, Z Wang, Y Guo, X Wang, Y Liu, Colloid Surface Physicochem Eng Aspect 446 (2014) 1–7, https://doi.org/10.1016/j
[37] L Li, S Liu, T Zhu, J Environ Sci 22 (2010) 1273–1280, https://doi.org/