JIS H 4000 2014 Aluminium And Aluminium Alloy Sheets, Strips And Plates

Describes rolled a aluminium and aluminium alloy sheets, strips, plates, clad plates and disks. Introduction 1 Scope 2 Normative references 3 Terms and definitions 4 Alloy numbers, classes and symbols 5 Quality 6 Dimensions and dimensional tolerances 7 Tests 8 Inspection 9 Marking Annex JA (informative) Comparison table between JIS and corresponding International Standards Bibliography

Trang 1

Aluminium and aluminium alloy

sheets, strips and plates

Trang 2

Date of Establishment: 1970-05-01

Date of Revision: 2014-03-20

Date of Public Notice in Official Gazette: 2014-03-20

Investigated by: Japanese Industrial Standards Committee

Standards Board Technical Committee on Non-Ferrous Metals

JIS H 4000: 2014, First English edition published in 2015-04

Translated and published by: Japanese Standards Association

Mita MT Building, 3-13-12, Mita, Minato-ku, Tokyo, 108-0073 JAPAN

In the event of any doubts arising as to the contents, the original JIS is to be the final authority

Trang 3

Page

Introduction··· ···1

1 Scope··· ···1

2 Normative references 1

3 Terms and definitions 3

4 Alloy numbers, classes and symbols ···4

5 Quality ···6

5.1 Appearance 6

5.2 Chemical composition ···7

5.3 Mechanical properties ···11

5.4 Electrical conductivity ···45

6 Dimensions and dimensional tolerances··· 46

6.1 Preferred dimensions for sheets ···46

6.2 Thickness of skin material of clad plates ···46

6.3 Thickness tolerances for sheets, strips, plates, clad plates, and disks 47

6.4 Width tolerances for sheets, strips, plates and clad plates ···51

6.5 Tolerances on diameter of disks ···52

6.6 Length tolerances for sheets, plates and clad plates 53

6.7 Squareness of sheets, plates and clad plates 54

6.8 Lateral curvature of sheets, strips, plates and clad plates ···54

6.9 Deviation from flatness of sheets, plates and clad plates ···56

7 Tests ···59

7.1 Chemical analysis··· 59

7.2 Tensile test ···59

7.3 Bend test··· ···60

7.4 Electrical conductivity test ···60

7.5 Thickness measurement test of skin material of clad plates ···60

8 Inspection 60

9 Marking ···62

Annex JA (informative) Comparison table between JIS and corresponding International Standards 63

Trang 4

This translation has been made based on the original Japanese Industrial Standard revised by the Minister of Economy, Trade and Industry, through deliberations at the Japanese Industrial Standards Committee as the result of proposal for revision of Japanese Industrial Standard submitted by Japan Aluminium Association (JAA)! Japanese Standards Association (JSA) with the draft being attached, based on the provision of Article 12 Clause 1 of the Industrial Standardization Law applicable to the case of revision by the provision of Article 14

relevant provisions of Article 19 Clause 1, etc of the Industrial Standardization Law until March 19, 2015

Attention is drawn to the possibility that some parts of this Standard may conflict with patent rights, applications for a patent after opening to the public or utility model rights The relevant Minister and the Japanese Industrial Standards Committee are not responsible for identifying any of such patent rights, applications for a patent after opening to the public or utility model rights

Trang 5

strips and plates

Introduction

This Japanese Industrial Standard has been prepared based on the first edition of

ISO 209 published in 2007, the second edition of ISO 6361-1 published in 2011, the

of ISO 6361-5 published in 2011 with some modifications of the technical contents

The portions with continuous sidelines or dotted underlines are the matters in which the contents of the corresponding International Standards have been modified A list

of modifications with the explanations is given in Annex JA

1 Scope

This Standard specifies rolled aluminium and aluminium alloy sheets, strips, plates,

~~~_~ p~~~~~_ and ~~_~~_~_ (hereafter referred to as "sheets", "strips", "plates", "~~~~ p~~~~~:'

and "disks")

NOTE: The International Standards corresponding to this Standard and the

sym-bol of degree of correspondence are as follows:

ISO 209: 2007 Aluminium and aluminium alloys-Chemical composition ISO 6361-1: 2011 Wrought aluminium and aluminium alloys-Sheets,

strips and plates-Part 1: Technical conditions for inspection and delivery

ISO 6361-2: 2011 Wrought aluminium and aluminium alloys-Sheets,

strips and plates-Part 2: Mechanical properties

strips and plates-Part 3: Strips: Tolerances on shape and dimensions

strips and plates-Part 4: Sheets and plates-Tolerances on shape and dimensions

strips and plates-Part 5: Chemical composition (overall evaluation: MOD)

The symbols which denote the degree of correspondence in the contents

21-1

2 Normative references

The following standards contain provisions which, through reference in this text,

Trang 6

JIS H 0001 Aluminium, magnesium and their alloys-Temper designation

NOTE: Corresponding International Standard: ISO 2107 Aluminium and

alu-minium alloys-Wrought products-Temper designations (MOD)

JIS H 0321 General rules for inspection of non-ferrous metal materials

JIS H 0505 Measuring methods for electrical resistivity and conductivity of

JIS H 1307 Methods for inductively coupled plasma emission spectrometric analysis

of aluminium and aluminium alloys

JIS H 1351 General rules for chemical analysis of aluminium and aluminium alloy JIS H 1352 Methods for determination of silicon in aluminium and aluminium

JIS H 1363 Methods for determination of zirconium in aluminium alloys

JIS H 1364 Methods for determination of bismuth in aluminium and aluminium

alloys

JIS H 1365 Methods for determination of boron in aluminium and aluminium alloys

Trang 7

JIS H 1368 Method for determination of gallium in aluminium and aluminium

alloys

ASTM G34 Standard Test Method for Exfoliation Corrosion Susceptibility in 2XXX

and 7XXX Series Aluminum Alloys (EXCO Test)

ASTM G47 Standard Test Method for Determining Susceptibility to Stress-Corrosion

Cracking of 2XXX and 7XXX Aluminum Alloy Products

ASTM G66 Standard Test Method for Visual Assessment of Exfoliation Corrosion

Susceptibility of 5XXX Series Aluminum Alloys Products (ASSET Test)

3 Terms and definitions

For the purpose of this Standard, the following terms and definitions apply

3.1 sheet

generally, a rolled product that is rectangular in cross-section with thickness 0.20 mm

or over up to and including 6 mm, which is sheared or sawed and supplied in straight lengths

3.2 strip

generally, a rolled product of rectangular cross-section with thickness 0.20 mm or over

up to and including 6 mm, supplied in coils with slit edges

A "strip" is sometimes called a "coil"

NOTE: For definition of sheets and strips, those with a thickness 0.15 mm or over

generally, a rolled product that is rectangular in cross-section and with thickness over

6 mm, with sheared or sawn edges and supplied in straight lengths

Trang 8

4 Alloy numbers, classes and symbols

The alloy numbers, classes and symbols shall be as given in table 1 The product symbol shall consist of the symbol shown in the table, and the symbol of temper grade suffixed to it

Table 1 Alloy numbers, classes and symbols

Alloy

Used for reflection plates, lighting fixtures, ornaments, tanks for

1060 - A1060P b) Pure aluminium for conductor having high electrical conductivity

Used for bus bars and others

Having a relatively low strength but excellent formability,

Used for general vessels, architectural materials, electrical appliances, various containers, printing boards and others

- A2014P A high strength heat-treated alloy In the case of clad plate, 6003

- A2014PC c) aircraft materials, various construction materials and others

2014

for aircrafts materials, various construction materials and others

weldability Used for aerospace instruments and others

- A2024P Higher in strength than 2017 and excellent in machinability Clad

- A2024PC c) surface Used for aircraft materials, various construction materials

and others

Used for general vessels, architectural materials, ship materials,

Trang 9

Used for architectural material, coloured aluminium, caps and others

Equivalent in strength to 3003, excellent in corrosion resistance, weldability and machinability

U sed for exterior and interior materials of buildings, interior material of vehicles and others

Equivalent in strength to 3003 A high brightness can be obtained

by bright processing such as chemical or electrolytic polishing followed by anodic oxidation processing Excellent in formability and corrosion resistance Used for ornaments, kitchen utensils, name plates and others

Equivalent in strength to 5052, excellent in corrosion resistance and formability Used for beverage can material and others

Alloy having a strength between those of 5052 and 5182 Excellent

in corrosion resistance and formability

Used for beverage can material and others

Used for architectural materials, refrigerating machines, electronics devices and others

Representative alloy having a medium strength Excellent in corrosion resistance, formability and weldability Used for ship materials, vehicle materials, architectural materials, beverage cans and others

Alloy having strength between those of 5052 and 5083 Excellent

in corrosion resistance, formability and weldability Used for ship materials, vehicle materials, pressure vessels and others

An alloy of 5154, but with restrained decomposition of hydrogen peroxide achieved by limiting the content of impurities, the other characteristics being the same as those of 5154 Used for hydrogen peroxide vessels and others

Higher in strength than 5052, excellent in corrosion resistance, formability and weldability Used for automobile wheels and others

Alloy having strength intermediate between those of 5052 and 5454

U sed for welding structural materials with higher strength, pressure vessels, ship materials and others

Approximately equivalent in strength to 5083, and excellent in corrosion resistance and formability Used for beverage cans, and others

Alloy having the highest strength among non-he at-treated alloys Excellent in corrosion resistance and weldability Used for ship

Trang 10

Table 1 (concluded)

Alloy

Welding structural alloy with higher strength than that of 5154

Used for ship materials, pressure vessels, magnetic disks and others

conductivity Used for bus bars and others

Excellent in corrosion resistance Mainly used for structural

6061 - A6061P materials for bolt or rivet jointing Used for ship and vehicle

materials, ground constructions and others

corrosion resistance Used for skis and others

Used for vehicles, ground constructions and others

- A7075P Alloy having the highest strength among aluminium alloys Clad

7075

A7075PC c)

plate has an improved corrosion resistance by cladding 7072 on the

Approximately equivalent in strength to 7075, excellent in

and others

skis and others

and corrosion resistance

packaging and others

Notes a) Parenthesized alloy numbers are old alloy numbers

Use of old alloy numbers should be avoided as far as possible

d) The utilization of A5083PS shall be limited to a side wall plate, annular plate and knuckle plate of storage tank for liquefied natural gas

5 Quality

5.1 Appearance

Trang 12

-

-Core

0.10 max 0.12 max 0.03 max

0.15 max 0.15 max 0.03 max

0.20 max 0.25 max 0.04 max

0.25 max 0.35 max 0.05 max

0.25 max 0.40 max 0.05 max

0.03 max 0.03 max - 0.04 max VO.05 max

0.03 max 0.03 max - 0.05 max VO.05 max

0.05 max 0.05 max - 0.05 max VO.05 max

0.05 max 0.05 max - 0.07 max

-0.8 max 0.8 to 1.5 0.35 max 0.20 max

-0.40 to 1.2 0.20 to 0.8 0.10 max 0.25 max Ni 0.10 max.,

0.10 max 0.05 max 0.15 max

0.05 max 0.05 max 0.15 max

- 0.03 max

-0.15 max 0.05 max 0.15 max

0.15 max 0.05 max 0.15 max

0.10 max 0.05 max 0.15 max

0.15 max 0.05 max 0.15 max

- 0.05 max 0.15 max

0.02 to 0.10 0.05 max 0.15 max

0.15 max 0.05 max 0.15 max

Trang 13

- - -

-

-0.6 max 0.7 max 0.05 to 0.20 1.0 to 1.5 0.50 max 0.7 max 0.10 max 0.9 to 1.5 0.6 max 0.7 max 0.05 max 1.0 to 1.5 0.30 max 0.7 max 0.25 max 1.0 to 1.5

0.6 max 0.8 max 0.05 to 0.25 0.8 to 1.4

0.6 max 0.7 max 0.30 max 1.0 to 1.5 0.6 max 0.7 max 0.30 max 0.30 to 0.8 0.30 max 0.7 max 0.20 max 0.20 max

0.15 max 0.25 max 0.20 max 0.20 max

0.40 max 0.50 max 0.15 max 0.10 to 0.50 0.20 max 0.35 max 0.15 max 0.20 to 0.50 0.40 max 0.7 max 0.20 max 0.10 max

0.25 max 0.40 max 0.10 max 0.10 max

Si + Fe 0.45 max 0.05 max 0.01 max

0.25 max 0.40 max 0.10 max 0.50 to 1.0 0.40 max 0.40 max 0.10 max 0.50 max

0.25 max 0.40 max 0.10 max 0.50 to 1.0 0.20 max 0.35 max 0.15 max 0.15 max

0.20 max 0.35 max 0.15 max 0.20 to 0.50 0.40 max 0.40 max 0.10 max 0.40 to 1.0 0.40 max 0.50 max 0.10 max 0.20 to 0.7 0.30 to 0.7 0.50 max 0.10 max 0.03 max

-

0.10 max 0.05 max 0.15 max

0.20 max 0.05 max 0.15 max

0.05 max 0.05 max 0.15 max

0.20 max 0.05 max 0.15 max

0.15 max 0.05 max 0.15 max

0.20 max 0.05 max 0.15 max

0.10 max 0.05 max 0.15 max

0.15 max 0.05 max 0.15 max

- 0.03 max 0.10 max

0.15 max 0.05 max 0.15 max

0.10 max 0.05 max 0.15 max

Remainder Remainder Remainder Remainder

Remainder

Remainder Remainder Remainder

Remainder

Remainder Remainder Remainder Remainder Remainder Remainder Remainder Remainder Remainder Remainder Remainder Remainder Remainder Remainder Remainder Remainder

::r:

Trang 14

7475 - 0.10 max 0.12 max 1.2 to 1.9 0.06 max 1.9 to 2.6 0.18 to 0.25 5.2 to 6.2 - 0.06 max 0.05 max 0.15 max Remainder

7178 - 0.40 max 0.50 max 1.6 to 2.4 0.30 max 2.4 to 3.1 0.18 to 0.28 6.3 to 7.3 - 0.20 max 0.05 max 0.15 max Remainder

80llA - 0.40 to 0.8 0.50 to 1.0 0.10 max 0.10 max 0.10 max 0.10 max 0.10 max - 0.05 max 0.05 max 0.15 max Remainder

8021 - 0.15 max 1.2 to 1.7 0.05 max - - - - 0.05 max 0.15 max Remainder

8079 - 0.05 to 0.30 0.7 to 1.3 0.05 max - - - 0.10 max - - 0.05 max 0.15 max Remainder

are the total sums of these unlisted "Each" elements Unlisted elements may be analysed at the discretion of the manufacturer when presence of such elements is expected or when, in the routine analysis, there is an indication that such elements will exceed the specified "Others" value

o

I -l

~

Trang 15

5.3 Mechanical properties

5.3.1 Mechanical properties of sheets, strips, plates and disks

The mechanical properties (tensile strength, proof stress, elongation and bending) of the sheets, strips, plates and disks, when tested in accordance with 7.2 and 7.3, shall

-

-satisfy the requirements given in table 3 Mechanical properties for the products exceeding the range of thickness specified in table 3 shall be agreed upon between the purchaser and the supplier

The application of proof stress and bending is as follows

a) Proof stress Proof stress for alloys AI085P, AI080P, AI070P, AI060P, AI050P, AII00P, A1200P, AII00AP(AINOOP), AI230AP(AIN30P), A3003P, A3103P,

-

-A3203P, A3004P, A3104P, A3005P, A3105P, A5005P, A5052P and A6101P shall be applied only when requested by the purchaser

b) Bending The bend test shall be carried out only when requested by the purchaser

When a bend test is carried out, cracks shall not be generated on the outside of the bend of the sheet, strip, plate, or disk

Table 3 Mechanical properties of sheets, strips, plates and disks

Symbol Temper grade Thickness Tensile strength Proof stress Elongation b) Thickness Inside

70 min 35 min 15 min

and incl 13.0 H112 Over 13.0 up to 60 min 25 min 20 min - - -

and incl 25.0 Over 25.0 up to

and incl 75.0 0.2 or over up to

- 15 min

- 20 min

- 25 min

Over O.B up to and incl 95 - and incl 6.0 itself

AI070P and incl 1.3

Over 1.3 up to

15 min 35 min

15 min 30 min

- 2 min

- 3 min

Trang 16

Table 3 (continued)

- 2 min

3 min 0.2 or over up to Thickness H14 and incl 0.8 85 or over up to - and incl 0.8 x 0.5 H24d) Over 0.8 up to and incl 120 - Over 0.8 up to Thickness

and incl 1.3 65 min 4 min and incl 6.0 xl

Over 1.3 up to

65 min 5 min

65 min 6 min

and incl 12.0

A1080P and incl 0.5

A1070P Over 0.5 up to 2 min 0.2 or over up to Thickness

H16 and incl 0.8 100 or over up to - and incl 0.8 xl

H26d) Over 0.8 up to and incl 135 - Over 0.8 up to Thickness

and incl 1.3 75 min 3 min and incl 4.0 x 1.5 Over 1.3 up to

75 min 4 min

1 min

2 min

and incl 0.8 H18

H112 and incl 13.0 6.0 or over up to Thickness

and incl 25.0 60 min 25 min 16 min

A1060P Over 25.0 up to 55 min 20 min 22 min

- and incl 50.0

0.8 or over up to

4 min

and incl 1.3 H14 Over 1.3 up to

85 min 65 min 5 min 0.8 or over up to Thickness

Over 2.9 up to

6 min

and incl 13.0 A1050P H112 Over 13.0 up to 70 min 35 min 16 min - - -

and incl 75.0

Trang 17

- 20 min

and incl 0.8

0 Over 0.8 up to 60 or over up to 20 min 25 min

and incl 1.3 and incl 100 Over 1.3 up to

-20 min 30 min

20 min 28 min

- 2 min

- 3 min

4 min

H12 and incl 0.8 80 or over up to

-H22d ) Over 0.8 up to and incl 120

-and incl 1.3 65 min 6 min

Over 1.3 up to

65 min 8 min

65 min 9 min

- 1 min

and incl 0.3

3 min

-H24d) Over 0.8 up to and incl 125

Over 1.3 up to

75 min 5 min

75 min 6 min

- 1 min

- 2 min

H26d) Over 0.8 up to and incl 145

Over 1.3 up to

85 min 4 min

1 min

2 min

and incl 0.8 H18

0.2 or over up to Flat on and incl 0.8 itself Over 0.8 up to Thickness and incl 6.0 x 0.5

0.2 or over up to Thickness and incl 0.8 x 0.5 Over 0.8 up to Thickness and incl 6.0 x 1

0.2 or over up to Thickness and incl 4.0 x2

Trang 18

-Table 3 (continued)

22 min

-and incl 1.5 Over 1.5 up to

26 min

-0 and incl 3.0 65 or over up to 20 min

-Over 6.0 up to

35 min

32 min 32 min

2 min

3 min

4 min

and incl 1.5 105 or over up to H24

Over 1.5 up to and incl 145 75 min - -

Over 3.0 up to

8 min

1 min

2 min

95 min 50 min 9 min

90 min 50 min 9 min

and incl 13.0 H1l2

-85 min 35 min 14 min

AllOOP and incl 50.0

AllOOAP Over 50.0 up to 80 min 25 min 20 min

~~.~~.QQ~~ and incl 75.0

-A1230AP and incl 0.5

-and incl 0.8

0 Over 0.8 up to 75 or over up to 25 min 22 min 0.2 or over up to Flat on

and incl 1.3 and incl 105 - and incl 6.0 itself Over 1.3 up to

30 min

28 min 25 min

and incl 75.0

Trang 19

Symbol Temper grade Thickness

0.2 or over up to and incl 0.3 Over 0.3 up to and incl 0.5 Over 0.5 up to H12 and incl 0.8

H22d ) Over 0.8 up to

and incl 1.3 Over 1.3 up to and incl 2.9 Over 2.9 up to and incl 12.0 0.2 or over up to and incl 0.3 Over 0.3 up to and incl 0.5 Over 0.5 up to AII00P H14 and incl 0.8

H26d ) Over 0.8 up to

and incl 1.3 Over 1.3 up to and incl 4.0 0.2 or over up to and incl 0.5 Over 0.5 up to and incl 0.8 H18

Over 0.8 up to and incl 1.3 Over 1.3 up to and incl 3.0 0.4 or over up to and incl 0.5

oe) Over 0.5 up to

and incl 13.0 Over 13.0 up to and incl 25.0 A2014P 0.4 or over up to

and incl 0.5 Over 0.5 up to and incl 6.0 T3

Over 6.0 up to and incl 6.3 Over 6.3 up to and incl 12.0

Tensile test Tensile strength Proof stress Elongation b)

0.2 or over up to Thickness and incl 6.0 xI

0.2 or over up to Thickness and incl 4.0 x2

-004 or over up to Thickness

and incl 1.6 x 0.5 Over 1.6 up to Thickness and incl 2.9 xI Over 2.9 up to Thickness and incl 6.0 x 1.5

004 or over up to Thickness

and incl 0.5 x 1.5 Over 0.5 up to Thickness and incl 1.6 x 2.5 Over 1.6 up to Thickness and incl 2.9 x3 Over 2.9 up to Thickness and incl 6.0 x 3.5

Trang 20

0.4 or over up to

395 min 240 min 0.4 or over up to Thickness

Over 0.5 up to

395 min 240 min Over 0.5 up to Thickness

T4

Over 6.0 up to 14 min - Over 1.6 up to Thickness and incl 6.3 400 min 250 min and incl 2.9 x3 Over 6.3 up to

6.0 or over up to

Over 0.5 up to

440 min 390 min 6 min and incl 0.5 x3

T6 Over 1.0 up to 440 min 390 min 7 min and incl 1.6 x 3.5

A2014P

Over 6.0 up to

450 min 395 min 7 min and incl 2.9 x 4.5

and incl 1.0 T62g) Over 1.0 up to

460 min 405 min 7 min 6 min

and incl 50.0 T651

405 min 380 min - 1 min

and incl 100.0

Trang 21

0

and incl 12.0 Over 12.0 up to and incl 12.5 Over 12.5 up to and incl 25.0 0.35 or over up

to and incl 0.5 Over 0.5 up to and incl 1 0 Over 1.0 up to T3 and incl 1.6

T4 Over 1.6 up to

to and incl 0.5 A2014AP Over 0.5 up to

and incl 1 0 Over 1.0 up to and incl 1 6 T6

Over 1.6 up to and incl 6.0 Over 6.0 up to and incl 6.3 Over 6.3 up to and incl 12.0 6.0 or over up to and incl 6.3 Over 6.3 up to and incl 12.0 Over 12.0 up to and incl 12.5 Over 12.5 up to and incl 25.0 T451D

Over 25.0 up to and incl 40.0 Over 40.0 up to and incl 50.0 Over 50.0 up to and incl 60.0 Over 60.0 up to and incl 80.0

-395 min 240 min 14 min

-400 min 250 min 14 min

-400 min 250 min 14 min 12 min

400 min 250 min - 10 min

400 min 250 min - 8 min

395 min 250 min - 7 min

390 min 240 min - 7 min

Trang 22

and incl 25.0 A2014AP T651 Over 25.0 up to 460 min 405 min - 5 min - -

450 min 390 min - 3 min

435 min 380 min - 1 min

405 min 350 min - 1 min

and incl 100.0 0.4 or over up to 0.4 or over up to Thickness

110 max Over 2.9 up to Thickness and incl 25.0

and incl 6.0 x 1.5 0.4 or over up to

12 min 0.4 or over up to Thickness

Over 0.5 up to

T3

6.0 or over up to

and incl 50.0 T351

Over 0.5 up to

T4

6.0 or over up to

12 min

and incl 50.0 T451

Over 80.0 up to

10 min

and incl 100.0

Trang 23

a) mm

0.4 or over up to and incl 0.5 Over 0.5 up to and incl 1 6 A2017P T42g) Over 1.6 up to

to and incl 3.2

0 Over 3.2 up to

and incl 6.0 Over 6.0 up to and incl 12.0 0.35 or over up

to and incl 6.0 T4

Over 6.0 up to and incl 12.0 6.0 or over up to A2017AP and incl 12.0

Over 12.0 up to and incl 25.0 Over 25.0 up to and incl 40.0 T451 Over 40.0 up to

and incl 60.0 Over 60.0 up to and incl 80.0 Over 80.0 up to and incl 120.0 Over 120.0 up to and incl 150.0 0.5 or over up to and incl 13.0

oe)

Over 13.0 up to and incl 50.0 0.5 or over up to T31 h) and incl 1 0

Over 1.0 up to A2219P

and incl 6.5 6.5 or over up to and incl 12.5 Over 12.5 up to T351 i) and incl 50.0

Over 50.0 up to and incl 80.0 Over 80.0 up to and incl 100.0

355 min - 12 min

-355 min 195 min 15 min

390 min 250 min - 12 min

385 min 240 min - 10 min

370 min 240 min - 8 min

350 min 240 min - 4 min

-305 min 195 min 10 min

Trang 24

and incl 12.5 T37j) Over 12.5 up to

6 min

7 min

and incl 6.5 T62g) Over 6.5 up to

8 min

7 min

6 min

and incl 1.0 T81

A2219P 6.5 or over up to 425 min 315 min 8 min

and incl 50.0 T851 Over 50.0 up to 425 min 310 min 6 min 5 min - -

405 min 295 min - 4 min

395 min 290 min - 3 min

and incl 60.0 T87

420 min 340 min - 2 min

and incl 120.0

004 or over up to

140 max 12 min 004 or over up to Flat on

Over 0.5 up to

140 max 12 min Over 0.5 up to Thickness

Over 13.0 up to

95 max 12 min Over 1.6 up to Thickness

Trang 25

a) mm

0.4 or over up to and incl 0.5 T3

Over 0.5 up to and incl 6.5 6.5 or over up to and incl 13.0 Over 13.0 up to and incl 25.0 Over 25.0 up to and incl 40.0 Over 40.0 up to T351 i) and incl 50.0

Over 50.0 up to and incl 80.0 Over 80.0 up to and incl 100.0 Over 100.0 up to and incl 120.0 Over 120.0 up to and incl 150.0 0.4 or over up to and incl 0.5 Over 0.5 up to T361 k) and incl 1 6

Over 1.6 up to and incl 6.5 A2024P Over 6.5 up to

and incl 12.0 0.4 or over up to and incl 0.5 T4

Over 0.5 up to and incl 6.0 0.4 or over up to and incl 0.5 Over 0.5 up to T42g ) and incl 6.5

Over 6.5 up to and incl 13.0 Over 13.0 up to and incl 25.0 0.4 or over up to and incl 0.5 T62g) Over 0.5 up to

and incl 13.0 Over 13.0 up to and incl 25.0 T81 0.25 or over up

to and incl 6.5 6.5 or over up to and incl 13.0 Over 13.0 up to

395 min 285 min - 2 min

380 min 260 min - 2 min

460 min - 8 min

-430 min 265 min 12 min

-0.4 or over up to Thickness and incl 1.6 x3 Over 1.6 up to Thickness and incl 2.9 x4 Over 2.9 up to Thickness and incl 6.0 x5

0.4 or over up to Thickness and incl 0.5 x2 Over 0.5 up to Thickness and incl 2.9 x3 Over 2.9 up to Thickness and incl 6.0 x4

Trang 26

and incl 1.6 A2024P T861

455 min 395 min - 5 min

to and incl 50.0 Over 50.0 up to

450 min 395 min - 5 min

and incl 80.0 A2124P T851 Over 80.0 up to 450 min 385 min - 4 min - -

440 min 380 min - 4 min

435 min 370 min - 4 min

- and incl 50.0

Over 50.0 up to

- 18 min

35 min 20 min

and incl 0.8

0 Over 0.8 up to 95 or over up to 35 min 22 min 0.2 or over up to Flat on

and incl 1.3 and incl 135 - and incl 6.0 itself Over 1.3 up to

35 min 25 min

and incl 6.5 A3003P Over 6.5 up to and incl 75.0 35 min 23 min

- 4 min

85 min 8 min

85 min 9 min

and incl 12.0

Trang 27

115 min 2 min

115 min 3 min

H24d) Over 1.3 up to and incl 180

Over 2.9 up to

115 min 5 min

Over 1.3 up to

145 min 4 min

1 min

2 min

and incl 0.8 H18

Over 0.8 up to 180 min 165 min

Over 1.3 up to

4 min

17 min

19 min

21 min

Over 3.0 up to and incl 130

-Over 6.0 up to

28 min

2 min

3 min

-H14 and incl 3.0 140 or over up to 120 min

-Over 6.0 up to

5 min

Bend test c)

Thickness Inside

mm radius

0.2 or over up to Thickness and incl 2.9 xI Over 2.9 up to Thickness and incl 6.0 x 1.5

0.2 or over up to Thickness and incl 1.3 x2 Over 1.3 up to Thickness and incl 2.9 x 2.5 Over 2.9 up to Thickness and incl 4.0 x3

Trang 28

4 min

and incl 1.5 H24 Over 1.5 up to 140 or over up to 110 min 5 min - - -

1 min

2 min

- 10 min

14 min 0.2 or over up to Flat on and incl 0.8 155 or over up to - and incl 0.8 itself

0

Over 0.8 up to and incl 195 - Over 0.8 up to Thickness and incl 1.3 60 min 16 min and incl 3.0 x 0.5 Over 1.3 up to

60 min 18 min

- 3 min

H22d) Over 0.8 up to 195 or over up to 145 min 4 min and incl 0.8 x 0.5

and incl 1.3 and incl 245 - Over 0.8 up to Thickness H32

and incl 3.0 145 min 5 min

0.2 or over up to

- 1 min

and incl 0.5 H14 Over 0.5 up to 3 min 0.2 or over up to Thickness A3004P and incl 0.8 225 or over up to - and incl 0.8 x 1 A3104P H24d) Over 0.8 up to and incl 265 - Over 0.8 up to Thickness

- 1 min

and incl 0.5 H16 Over 0.5 up to 2 min 0.2 or over up to Thickness

and incl 0.8 245 or over up to - and incl 0.8 x2 H26d)

Over 0.8 up to and incl 285 - Over 0.8 up to Thickness H36

and incl 1.3 195 min 3 min and incl 3.0 x 2.5 Over 1.3 up to

195 min 4 min

and incl 3.0 H18

and incl 0.8 and incl 165 - - and incl 1.6 itself

Trang 29

1 min

0.3 or over up to

- 1 min

and incl 0.8 H18

0 Over 0.5 up to 100 or over up to 40 min 15 min

-17 min

3 min

and incl 0.5 H12 Over 0.5 up to 130 or over up to 105 min 4 min

-4 min

6 min

and incl 0.5 H22 Over 0.5 up to 130 or over up to 105 min 6 min -

7 min

1 min

and incl 0.5 A3105P H14 Over 0.5 up to 150 or over up to

4 min

and incl 0.5 H24 Over 0.5 up to 150 or over up to 120 min 4 min

-5 min

1 min

2 min

Bend test c)

Thickness Inside

mm radius

0.3 or over up to Thickness and incl 1.6 xl

0.3 or over up to Thickness and incl 0.8 x 1.5 Over 0.8 up to Thickness and incl 1.6 x2 0.3 or over up to Thickness and incl 0.8 x2 Over 0.8 up to Thickness and incl 1.6 x3

-0.2 or over up to Flat on and incl 0.5 itself Over 0.5 up to Flat on and incl 1.5 itself Over 1.5 up to Thickness and incl 3.0 x 0.5 0.2 or over up to Thickness and incl 0.5 x 1.5 Over 0.5 up to Thickness and incl 1.5 x 1.5 Over 1.5 up to Thickness and incl 3.0 x 1.5

-0.2 or over up to Thickness and incl 0.5 x 2.5 Over 0.5 up to Thickness and incl 1.5 x 2.5 Over 1.5 up to Thickness and incl 3.0 x 2.5 0.2 or over up to Thickness and incl 0.5 x 2.5 Over 0.5 up to Thickness and incl 1.5 x 2.5 Over 1.5 up to Thickness and incl 3.0 x 2.5

Trang 30

1 min

and incl 3.0

and incl 0.5 H28

0.2 or over up to

1 min

and incl 0.5 H19

16 min

19 min

-0 and incl 1.3 105 or over up to 35 min 0.5 or over up to Flat on

Over 1.3 up to and incl 145 and incl 6.0 itself

-Over 2.9 up to

22 min 20 min

2 min

and incl 1.3

H12 and incl 2.9 125 or over up to 95 min 0.5 or over up to Thickness

Over 2.9 up to and incl 165 - and incl 6.0 x 0.5

Over 4.0 up to

5 min

7 min

- 3 min

85 min 4 min

85 min 6 min

H22d) and incl 2.9 120 or over up to 0.5 or over up to Thickness

-H32 Over 2.9 up to and incl 155 and incl 6.0 x 0.5

and incl 4.0 85 min 7 min

Over 4.0 up to

85 min 8 min

85 min 9 min

and incl 12.0

Trang 31

2 min

3 min

H14 and incl 2.9 145 or over up to 120 min

Over 4.0 up to

4 min

5 min

3 min

4 min

5 min

H24d ) and incl 2.9 140 or over up to

H34 Over 2.9 up to and incl 180 105 min

Over 4.0 up to

5 min

-3 min

and incl 1.3 Over 1.3 up to and incl 3.0 0.5 or over up to

2 min

and incl 0.8 H38 Over 0.8 up to 180 min 165 min 2 min -

4 min

10 min

15 min

A5110AP

0 and incl 0.5 85 or over up to

0.5 or over up to Thickness and incl 2.9 xl Over 2.9 up to Thickness and incl 6.0 x 1.5

0.5 or over up to Thickness and incl 1.3 x2 Over 1.3 up to Thickness and incl 2.9 x 2.5 Over 2.9 up to Thickness and incl 4.0 x3 0.5 or over up to Thickness and incl 1.3 x2 Over 1.3 up to Thickness and incl 2.9 x 2.5 Over 2.9 up to Thickness and incl 4.0 x3

-0.2 or over up to Flat on and incl 6.0 itself

Trang 32

3 min

9 min

1 min

2 min

6 min

1 min

2 min

and incl 0.8 H18

- 10 min

and incl 80.0

Trang 33

17 min

19 min

and incl 3.0 130 or over up to

-0 Over 3.0 up to and incl 170 45 min

2 min

4 min

5 min

H22d) and incl 1.5 155 or over up to

110 min

H32 Over 1.5 up to and incl 195

Over 3.0 up to

10 min

2 min

and incl 0.5

Over 1.5 up to and incl 215 150 min

Over 3.0 up to

4 min

3 min

4 min

Over 3.0 up to

8 min

1 min

2 min

Over 1.5 up to and incl 235 170 min

Over 3.0 up to

3 min

2 min

3 min

-Bend test c)

Thickness Inside

mm radius

0.2 or over up to Flat on and incl 0.5 itself Over 0.5 up to Flat on and incl 1.5 itself Over 1.5 up to Thickness and incl 3.0 x 0.5

-0.2 or over up to Thickness and incl 0.5 x 1 Over 0.5 up to Thickness and incl 1.5 x 1 Over 1.5 up to Thickness and incl 3.0 x 1.5

-0.2 or over up to Thickness and incl 0.5 x 1.5 Over 0.5 up to Thickness and incl 1.5 x 1.5 Over 1.5 up to Thickness and incl 3.0 x2

Trang 34

-Over 1.5 up to

3 min

and incl 13.0 H112

- 14 min

65 min 15 min

65 min 17 min 0.2 or over up to Flat on

0 Over 0.8 up to 170 or over up to 65 min 17 min Over 0.8 up to Thickness

and incl 1.3 and incl 215 - and incl 2.9 x 0.5 Over 1.3 up to

Over 2.9 up to

65 min 19 min

65 min 18 min

H12

H22d) Over 0.8 up to 215 or over up to 155 min 5 min Over 0.8 up to Thickness

and incl 1.3 and incl 265 - and incl 2.9 xI H32

Over 1.3 up to

Over 2.9 up to

155 min 9 min

155 min 11 min

3 min

4 min

H24d) and incl 1.3 235 or over up to 180 min Over 0.8 up to Thickness

Over 1.3 up to and incl 285 - and incl 2.9 x 1.5 H34

and incl 2.9 6 min Over 2.9 up to Thickness

Trang 35

a) mm

0.2 or over up to H16 and incl 0.8

H26d)

H36 Over 0.8 up to

and incl 4.0 A5052P

0.2 or over up to H18 and incl 0.8

H38 Over 0.8 up to

and incl 3.0 H19 0.15 or over up

H39 to and incl 0.5

4.0 or over up to and incl 6.5 Over 6.5 up to and incl 13.0 H112

Over 13.0 up to and incl 50.0 Over 50.0 up to and incl 75.0 0.5 or over up to and incl 0.8 Over 0.8 up to

0 and incl 1.3

Over 1.3 up to and incl 2.9 Over 2.9 up to and incl 75.0 0.5 or over up to and incl 0.8 H12 Over 0.8 up to

H22d) and incl 1.3

Over 1.3 up to H32

and incl 6.5 Over 6.5 up to A5154P and incl 12.0

A5254P 0.5 or over up to

and incl 0.8 Over 0.8 up to H14 and incl 1.3

H24d) Over 1.3 up to

and incl 4.0 H34

Over 4.0 up to and incl 6.5 Over 6.5 up to and incl 12.0 0.5 or over up to and incl 0.8 H16 Over 0.8 up to

H26d) and incl 1.3

Over 1.3 up to H36

-0.5 or over up to Thickness and incl 0.8 xI Over 0.8 up to Thickness and incl 2.9 x 1.5 Over 2.9 up to Thickness and incl 6.0 x2

0.5 or over up to Thickness and incl 0.8 x 1.5 Over 0.8 up to Thickness and incl 2.9 x2 Over 2.9 up to Thickness and incl 6.0 x 2.5

Trang 36

-Over 2.9 up to

18 min 16 min

12 min

14 min

and incl 1.5 190 or over up to

0

Over 1.5 up to and incl 240 80 min - -

Over 3.0 up to

18 min

6 min

and incl 0.5 A5754P H24d) Over 0.5 up to 6 min

and incl 1.5 240 or over up to H34 Over 1.5 up to and incl 280 160 min - - -

Over 3.0 up to

8 min

3 min

4 min

-and incl 12.5 H112 Over 12.5 up to 290 min 130 min - 10 min - -

285 min 125 min - 10 min

and incl 80.0 1.2 or over up to 290 or over up to 130 or over up to

270 min 115 min - 12 min

265 min 105 min - 10 min

and incl 200.0 4.0 or over up to 315 or over up to

Trang 37

a) mm

2.5 or over up to and incl 4.0 Over 4.0 up to H3211)m) and incl 12.5

Over 12.5 up to and incl 40.0 Over 40.0 up to and incl 80.0 A5456P 1.6 or over up to

and incl 12.5 Over 12.5 up to and incl 30.0 H1161) Over 30.0 up to

and incl 40.0 Over 40.0 up to and incl 80.0 Over 80.0 up to and incl 110.0 H18 0.2 or over up to

and incl 40.0 Over 40.0 up to and incl 75.0 0.5 or over up to and incl 0.8 Over 0.8 up to

0 and incl 40.0

Over 40.0 up to and incl 80.0 Over 80.0 up to and incl 100.0 0.5 or over up to A5083P and incl 0.8

H22d) Over 0.8 up to

H32 and incl 2.9

Over 2.9 up to and incl 12.0 4.0 or over up to and incl 13.0 H3211)m) Over 13.0 up to

285 or over up to

200 min - 10 min

and incl 370

-315 min 230 min - 10 min

305 min 215 min - 10 min

285 min 200 min - 10 min

275 min 170 min - 10 min

and incl 345 and incl 200

0.5 or over up to Thickness and incl 1.3 x 2.5 Over 1.3 up to Thickness and incl 2.9 x3 Over 2.9 up to Thickness and incl 6.5 x4 Over 6.5 up to Thickness and incl 12.0 x5