Such requirements to be considered include, but are not limited to, the following: 4.1.1 Quantity feet, metres, or number of pieces, 4.1.2 Name of material stainless steel pipe, 4.1.3 Pr
Trang 1Designation: A 999/A 999M – 9801
Standard Specification for
This standard is issued under the fixed designation A 999/A 999M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision A number in parentheses indicates the year of last reapproval.
A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
1
This specification is under the jurisdiction of ASTM Committee A-1 A01 on Steel, Stainless Steel, and Related Alloys and is the direct responsibility of Subcommittee A01.10 on Alloy Steel Tubular Products.
Current edition approved Dec March 10, 1998 2001 Published May 2001 Originally published as A 999/A 999M – 98 Last previous edition A 999/A 999M – 98.
of the standard as published by ASTM is to be considered the official document.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
Trang 21 Scope
1.1 This specification2covers a group of general requirements that, unless otherwise specified in an individual specification, shall apply to the ASTM product specifications noted below
1.2 In the case of conflict between a requirement of a product specification and a requirement of this specification, the product specification shall prevail In the case of conflict between a requirement of the product specification or a requirement of this specification and a more stringent requirement of the purchase order, the purchase order shall prevail
Designa-tion 3
Seamless and Welded Steel Pipe for Low-Temperature Service
A 333/A 333M Seamless Ferritic Alloy-Steel Pipe for High Temperature
Service
A 335/A 335M Electric-Fusion-Welded Austenitic Chromium-Nickel Alloy
Steel Pipe for High-Temperature Service
A 358/A 358M Carbon and Ferritic Alloy Steel Forged and Bored Pipe for
High-Temperature Service
A 369/A 369M Seamless Austenitic Steel Pipe for Use With High Temperature
Central-Station Service
A 376/A 376M Welded Large Diameter Austenitic Steel Pipe for Corrosive
or High-Temperature Service
A 409/A 409M Welded, Unannealed Austenitic Stainless Steel Tubular
Products
A 778
Ferritic/Austenitic (Duplex) Stainless Steel Pipe Electric Fusion Welded with Addition of Filler Metal
A 928
Spray-Formed Seamless Ferritic/Austenitic Stainless Steel Pipe
A 949 Austenitic Chromium-Nickel-Silicon Alloy Steel Seamless
and Welded Pipe
A 954
1.3 The values stated in either inch-pound units or SI units are to be regarded separately as standard With the text, the SI units are shown in brackets The values stated in each system are not exact equivalents; therefore each system must be used independently of the other Combining values from the two systems may result in nonconformance with the specification The inch-pound units shall apply unless the “M” designation (SI) of the product specification is specified in the order
N OTE 1—The dimensionless designator NPS (nominal pipe size) is used in this standard for such traditional terms as “nominal diameter,” “size,”“ nominal bore,” and “nominal size”.
1.4 The following precautionary statement pertains only to the test method portion, Section 21, of this specification: This
standard does not purport to address all of the safety concerns, if any, associated with its use It is the responsibility of the user
of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior
to use.
2 Referenced Documents
2.1 ASTM Standards:
A 370 Test Methods and Definitions for Mechanical Testing of Steel Products4
A 700 Practices for Packaging, Marking, and Loading Methods for Steel Products for Domestic Shipment4
A 751 Test Methods, Practices, and Terminology for Chemical Analysis of Steel Products5
D 3951 Practice for Commercial Packaging6
E 29 Practice for Using Significant Digits in Test Data to Determine Conformance with Specifications7
E 213 Practice for Ultrasonic Examination of Metal Pipe and Tubing8
E 273 Practice for Ultrasonic Examination of Longitudinal Welded Pipe and Tubing8
E 309 Practice for Eddy-Current Testing Examination of Steel Tubular Products Using Magnetic Saturation8
E 426 Practice for Electromagnetic (Eddy-Current) Examination of Seamless and Welded Tubular Products, Austenitic Stainless Steel and Similar Alloys8
2 For ASME Boiler and Pressure Vessel Code applications see related Specification SA 999 in Section II of that Code.
3
These designations refer to the latest issue of the respective specifications See Annual Book of ASTM Standards, Vol 01.01.
4Annual Book of ASTM Standards, Vol 01.05.
5
Annual Book of ASTM Standards, Vol 01.03.
6Annual Book of ASTM Standards, Vol 15.09.
7
Annual Book of ASTM Standards, Vol 14.02.
8Annual Book of ASTM Standards, Vol 03.03.
Trang 3E 570 Practice for Flux Leakage Examination of Ferromagnetic Steel Tubular Products8
2.2 ANSI Standards:
B36.10 Welded and Seamless Wrought Steel Pipe9
B36.19 Stainless Steel Pipe9
2.3 Military Standards:
MIL-STD-163 Steel Mill Products, Preparation for Shipment and Storage10
MIL-STD-271 Nondestructive Testing Requirements for Metals10
MIL-STD-792 Identification Marking Requirements for Special Purpose Equipment10
2.4 Federal Standard:
Fed Std No 183 Continuous Identification Marking of Iron and Steel Products10
2.5 Steel Structures Painting Council:
SSPC-SP6 Surface Preparation Specification No 6 Commercial Blast Cleaning11
2.6 ASNT Standards:
SNT-TC-1A Recommended Practice for Personnel Qualification and Certification in Nondestructive Testing12
3 Process
3.1 The steel shall be made by a suitable process
3.2 If secondary melting, such as electroslag remelting or vacuum remelting, is used, the heat shall be defined as all of the ingots remelted from a single primary heat
3.3 When steels of different are sequentially strand cast, the resultant transition material shall be removed using an established procedure that positively separates the grades
3.4 If a specific type of melting is required by the purchaser, it shall be specified on the purchase order
4 Ordering Information
4.1 It is the responsibility of the purchaser to specify all requirements that are necessary for material ordered under the product specification and this specification Such requirements to be considered include, but are not limited to, the following:
4.1.1 Quantity (feet, metres, or number of pieces),
4.1.2 Name of material (stainless steel pipe),
4.1.3 Process, when applicable (seamless or welded),
4.1.4 Grade or UNS number,
4.1.5 Size (NPS and outside diameter and schedule number, average (nominal) wall thickness (see 8.1 and 9.1), or minimum wall thickness (see 8.2 and 9.1.1), or minimum inside diameter (see 10.1)),
4.1.6 Length (specific or random),
4.1.7 End finish,
4.1.8 Optional requirements,
4.1.9 Specific type of melting, if required (see 3.4),
4.1.10 Certified test report requirements,
4.1.11 Specification designation and date of issue, and
4.1.12 Special requirement or any supplementary requirements, or both
5 Chemical Composition
5.1 Chemical Analysis—Samples for chemical analysis and method of analysis shall be in accordance with Test Methods,
Practices, and Terminology A 751
5.2 Heat Analysis—An analysis of each heat of steel shall be made by the steel manufacturer to determine the percentages of
the specified elements If secondary melting processes are employed, the heat analysis shall be obtained from one remelted ingot
or the product of one remelted ingot of each primary melt The chemical composition thus determined, or that determined from
a product analysis made by the tubular product manufacturer shall conform to the requirements specified
5.3 Product Analysis—Product analysis requirements and options, if any, are contained in the product specification.
6 Mechanical Properties
6.1 Method of Mechanical Tests—The specimens and the mechanical tests required shall be in accordance with Test Methods
and Definitions A 370, especially Annex A2 thereof
9
Portions of these standards appear in ASTM Book of Standards, Vol 01.01 Full text of these standards is available from American National Standards Institute, 11 West
42nd St., 13th floor, New York, NY 10036.
10 Available from Standardization Documents Order Desk, Bldg 4 Section D, 700 Robbins Ave., Philadelphia, PA 19111-5094, Attn: NPODS.
11
This specification is under the jurisdiction of ASTM Committee A01 on Steel, Stainless Steel, and Related Alloys and is the direct responsibility of Subcommittee A01.10
on Alloy Steel Tubular Products.
Current edition approved March 10, 2001 Published May 2001 Originally published as A 999/A 999M – 98 Last previous edition A 999/A 999M – 98.
12 Available from American Society for Nondestructive Testing, 1711 Arlington Plaza, P.O Box 28518, Columbus, OH 43228–0518.
Trang 46.2 Specimens shall be tested at room temperature.
6.3 Small or subsize specimens as described in Test Methods and Definitions A 370 may be used only when there is insufficient material to prepare one of the standard specimens When using small or subsize specimens, the largest one possible shall be used
7 Tensile Requirements
7.1 The material shall conform to the requirements as to tensile properties in the individual product specification
7.2 The yield strength, when specified, shall be determined corresponding to a permanent offset of 0.2 % of the gage length or
to a total extension of 0.5 % of the gage length under load
7.3 If the percentage of elongation of any test specimen is less than that specified and any part of the fracture is more than3⁄4
in [19.0 mm] from the center of the gage length, as indicated by scribe marks on the specimen before testing, a retest shall be allowed
8 Permissible Variation in Weight for Seamless Pipe
8.1 Except as noted in 8.2, the weight of any length of seamless pipe NPS 12 and under shall not vary more than 10 % over the 3.5 % under that specified For sizes over NPS 12, the weight of any length of pipe shall not vary more than 10 % over and
5 % under that specified Unless otherwise specified, pipe of NPS 4 and smaller may be weighed in convenient lots; pipe in sizes larger than NPS 4 shall be weighed separately
8.2 Minimum Wall—When the wall thickness of the pipe is specified as minimum wall in the purchase order, the weight of any
length of seamless pipe shall not vary more than 16 % over that calculated in accordance with 13.3 Unless otherwise specified, pipe of NPS 4 and smaller may be weighed in convenient lots; pipe in sizes larger than NPS 4 shall be weighed separately
9 Permissible Variations in Wall Thickness
9.1 Seamless and Welded—Except as noted in 9.1.1, the minimum wall thickness at any point shall not be more than 12.5 %
under the nominal wall thickness specified The minimum wall thickness on inspection is shown in Table X1.1
9.1.1 Minimum Wall—When the wall thickness of the pipe is specified as minimum wall in the purchase order, there shall be
no variation under the specified wall thickness
9.2 Forged and Bored—The wall thickness shall not vary over that specified by more than1⁄8in [3.2 mm] There shall be no variation under the specified wall thickness
9.3 Cast—The wall thickness shall not vary over that specified by more than1⁄16in [1.6 mm] There shall be no variation under the specified wall thickness
10 Permissible Variations in Inside Diameter
10.1 Forged and Bored, and Cast—The inside diameter shall not vary under that specified by more than1⁄16in [1.6 mm] There shall be no variation over the specified inside diameter
11 Permissible Variation in Outside Diameter
11.1 Variations in outside diameter, unless otherwise agreed upon, shall not exceed the limits prescribed in Table 1 The tolerances on outside diameter include ovality except as provided for in 11.2 and 11.2.1 (See Note 2.)
11.2 For thin-wall pipe, defined as pipe having a wall thickness of 3 % or less of the outside diameter, the diameter tolerance
of Table 1 is applicable only to the mean of the extreme (maximum and minimum) outside diameter readings in any one cross-section
11.2.1 For thin-wall pipe the difference in extreme outside readings (ovality) in any one cross-section shall not exceed 1.5 %
of the specified outside diameter
N OTE 2—Thin-wall pipe usually develops significant ovality (out-of-roundness) during final annealing, straightening, or both The diameter tolerances
of Table 1 are usually not sufficient to provide for additional ovality expected in thin-wall pipe.
12 Permissible Variations in Length
12.1 Seamless and Welded (No Filler Metal Added)—If specific cut lengths of 24 ft [7.3 m] or less are ordered, no length of
TABLE 1 Permissible Variations in Outside Diameter
NPS Designator
Permissible Variations in Outside Diameter
1 ⁄ 8 -1 1 ⁄ 2 , incl 1 ⁄ 64 (0.015) 0.4 1 ⁄ 32 (0.031) 0.8 Over 1 1 ⁄ 2 to 4, incl 1 ⁄ 32 (0.031) 0.8 1 ⁄ 32 (0.031) 0.8 Over 4 to 8, incl 1 ⁄ 16 (0.062) 1.6 1 ⁄ 32 (0.031) 0.8 Over 8 to 18, incl 3 ⁄ 32 (0.093) 2.4 1 ⁄ 32 (0.031) 0.8 Over 18 to 26, incl 1 ⁄ 8 (0.125) 3.2 1 ⁄ 32 (0.031) 0.8 Over 26 to 34, incl 5 ⁄ 32 (0.156) 4.0 1 ⁄ 32 (0.031) 0.8 Over 34 to 48, incl 3 ⁄ 16 (0.187) 4.8 1 ⁄ 32 (0.031) 0.8
Trang 5pipe shall be under the length specified or more than1⁄4in [6 mm] over that specified.
12.1.1 Permissible variations in length for lengths greater than 24 ft [7.3 m] shall be subject to agreement between the manufacturer and purchaser
12.2 Forged and Bored, Cast, and Cast Cold-Wrought—If specific cut lengths are ordered, no length of pipe shall be under the
length specified or more than1⁄8in [3 mm] over that specified
12.3 For pipe ordered to random lengths, the lengths and variations shall be agreed upon between the manufacturer and purchaser
12.4 No girth welds are permitted unless agreed upon by the manufacturer and purchaser
13 Standard Weight (Weight per Unit Length)
13.1 A system of standard pipe sizes has been approved by the American National Standards Institute as ANSI B36.10 and B36.19 The standard sizes do not prohibit the production and use of other sizes of pipe produced to the various product specifications referenced in 1.1 (See Note 3.)
13.2 For nonstandard sizes of pipe, the calculated weight per foot shall be determined from the following equation:
where:
W = weight, lb/ft [kg/m],
D = specified or calculated (from specified inside diameter and wall thickness) outside diameter, in [mm], and
t = specified wall thickness, in (to 3 decimal places) [mm to 2 decimal places]
13.3 When minimum wall thickness is specified on the purchase order, the calculated weight per foot shall be determined using
Eq 1, obtaining from Table X1.1 the nominal wall thickness, t, corresponding to that minimum wall.
N OTE 3—The weights given in the American National Standards and the calculated weights given by Eq 1 are based on the weights for carbon steel pipe The weight of pipe made of ferritic stainless steels may be up to about 5 % less, and that made of austenitic stainless steel up to about 2 % greater than the values given.
14 Ends
14.1 Unless otherwise specified, the pipe shall be furnished with plain ends All burrs at the ends of the pipe shall be removed
15 Straightness
15.1 The finished pipe shall be reasonably straight
15.2 For metal-arc welded pipe, the maximum deviation from a 10-ft [3.0-m] straightedge placed so that both ends are in contact with the pipe shall be1⁄8in [3.2 mm] For metal-arc welded pipe with lengths shorter than 10 ft [3.0 m], this maximum deviation shall be prorated with respect to the ratio of the actual length to 10 ft [3.0 m]
16 Repair by Welding
16.1 Repair by welding of defects in seamless pipe (including centrifugally cast pipe and forged and bored pipe) and of plate defects in welded pipe and, when specifically stated by the product specification, weld seam defects in welded pipe shall be permitted subject to the approval of the purchaser and with the further understanding that the composition of the deposited filler metal shall be suitable for the composition being welded Defects shall be thoroughly chipped or ground out before welding and each repaired length shall be reheat treated or stress relieved as required by the applicable specification Each length of repaired pipe shall be nondestructively tested as required by the product specification
16.2 Repair welding shall be performed using procedures and welders or welding operators that have been qualified in accordance with the ASME Boiler and Pressure Vessel Code, Section IX
17 Retests
17.1 If the results of the certification tests of any lot do not conform to the requirements specified in the individual specification, retests may be made on additional lengths of pipe of double the original number from the same lot, each of which shall conform
to the requirements specified Only one retest of any lot will be permitted Nonconformance will be cause for the rejection of the lot
17.2 Any individual length of pipe that meets the test requirements is acceptable Individual lengths that do not conform to the test requirements may be resubmitted for test provided the reason for nonconformance is established and the nonconforming portion removed
18 Retreatment
18.1 If individual lengths of pipe selected to represent any lot fail to conform to the test requirements, the lot represented may
be reheat treated and resubmitted for test The manufacturer may reheat treat the pipe, but not more than twice, except with the approval of the purchaser
Trang 619 Test Specimens
19.1 Test specimens shall be taken from the ends of finished pipe prior to any forming operations, or being cut to length 19.2 Specimens cut either longitudinally or transversely shall be acceptable for the tension test
19.3 If any test specimen shows flaws or defective machining, the specimen may be discarded and another substituted
20 Flattening Test Requirements
20.1 Seamless and Centrifugally Cast Pipe—A section of pipe not less than 21⁄2in [63 mm] in length shall be flattened cold between parallel plates in two steps During the first step, which is a test for ductility, no cracks or breaks on the inside, outside,
or end surfaces, except as provided for in 20.3.4, shall occur until the distance between the plates is less than the value of H
calculated as follows:
where:
H = distance between flattening plates, in [mm],
t = specified wall thickness, in [mm],
D = specified outside diameter, outside diameter corresponding to specified ANSI pipe size, or outside diameter calculated by
adding 2t (as defined above) to the specified inside diameter in [mm], and
e = deformation per unit length (constant for a given grade of steel, 0.07 for medium carbon steel (maximum specified carbon 0.19 % or greater), 0.08 for ferritic alloy steel, 0.09 for austenitic steel, and 0.09 for low-carbon steel (maximum specified carbon 0.18 % or less))
During the second step, which is a test for soundness, the flattening shall be continued until the specimen breaks or the opposite walls of the pipe meet
20.2 Welded Pipe—A section of welded pipe not less than 4 in [100 mm] in length shall be flattened cold between parallel plates
in two steps The weld shall be placed at 90° from the direction of the applied force (at the point of maximum bending) During the first step, which is a test for ductility, no cracks or breaks on the inside or outside surfaces, except as provided for in 20.3.4,
shall occur until the distance between the plates is less than the value of H calculated by Eq 2 During the second step, which is
a test for soundness, the flattening shall be continued until the specimen breaks or the opposite walls of the pipe meet
20.3 Seamless, Centrifugally Cast, and Welded Pipe:
20.3.1 Evidence of laminated or defective material or weld that is revealed at any time during the entire flattening test shall be cause for rejection
20.3.2 Surface imperfections not evident in the test specimen before flattening, but revealed during the first step of flattening test, shall be judged in accordance with the finish requirements
20.3.3 Superficial ruptures resulting from surface imperfections shall not be a cause for rejection
20.3.4 When low D-to-t ratio tubular products are tested, because the strain imposed due to geometry is unreasonably high on the inside surface at the six and twelve o’clock locations, cracks at these locations shall not be cause for rejection if the D-to-t ratio
is less than 10
21 Nondestructive Test Requirements
21.1 When required by the applicable product specification or the purchase order, the pipe shall be tested by the hydrostatic test (see 21.2) or by the nondestructive electrical test (see 21.3)
21.2 Hydrostatic Test:
21.2.1 Except as provided in 21.2.2 and 21.2.3, each length of pipe shall be tested by the manufacturer to a hydrostatic pressure which will produce in the pipe wall a stress not less than 60 % of the minimum specified yield strength for ferritic alloy and stainless steel pipe, or 50 % of the specified minimum yield strength for austenitic alloy and stainless steel pipe and for ferritic/austenitic stainless steel pipe The test pressure or stress shall be determined by the following equation:
where:
P = hydrostatic test pressure in psi [MPa],
S = pipe wall stress in psi or [MPa],
t = specified wall thickness, nominal wall thickness according to specified ANSI schedule number, or 1.143 times the specified minimum wall thickness, in [mm], and
D = specified outside diameter, outside diameter corresponding to specified ANSI pipe size, or outside diameter calculated by
adding 2t (as defined above) to the specified inside diameter, in [mm].
21.2.1.1 The hydrostatic test pressure determined by the equation shall be rounded to the nearest 50 psi [0.5 MPa] for pressures below 1000 psi [7 MPa], and to the nearest 100 psi [1 MPa] for pressures 1000 psi [7 MPa] and above The hydrostatic test may
be performed prior to cutting to final length, or prior to upsetting, swaging, expanding, bending, or other forming operations 21.2.2 Regardless of pipe-wall stress-level determined by Eq 3, the minimum hydrostatic test pressure required to satisfy these
requirements need not exceed 2500 psi [17.0 MPa] for outside diameters (see D in 21.2) of 3.5 in [88.9 mm] or less, or 2800 psi
Trang 7[19.0 MPa] for outside diameters over 3.5 in [88.9 mm] This does not prohibit testing at higher pressures at the option of the manufacturer or as provided in 21.3
21.2.3 With concurrence of the manufacturer, a minimum hydrostatic test pressure in excess of the requirements of 21.2 or 21.1,
or both, may be stated on the order
21.2.4 The test pressure shall be held for a minimum of 5 s For welded pipe, the test pressure shall be held for a time sufficient
to permit the entire length of the welded seam to be inspected
21.2.5 The hydrostatic test may not be capable of testing the end portion of the pipe The length of pipe that cannot be tested shall be determined by the manufacturer and, when specified in the purchase order, reported to the purchaser
21.3 Nondestructive Electric Test:
21.3.1 Each pipe shall be examined with a nondestructive test in accordance with Practices E 213, E 309, E 426, or E 570 Unless specifically called out by the purchaser, the selection of the nondestructive electric test shall be at the option of the manufacturer Upon agreement between purchaser and manufacturer, Practice E 273 shall be employed in addition to one of the full periphery tests The range of pipe sizes that may be examined by each method shall be subject to the limitations in the scope
of the respective practices
21.3.2 The following information is for the benefit of the user of this specification:
21.3.2.1 The reference standards defined in 21.2.2-21.2.5 are convenient standards for calibration of nondestructive testing equipment The dimensions of these standards should not be construed as the minimum size imperfection detectable by such equipment
21.3.2.2 The ultrasonic testing (UT) can be performed to detect both longitudinally and circumferentially oriented defects It should be recognized that different techniques should be used to detect differently oriented imperfections The examination may not detect short deep defects
21.3.2.3 The eddy-current testing (ET) referenced in this specification, (see Practices E 426 and E 309), has the capability of detecting significant discontinuities, especially of the short abrupt type The sensitivity of this test decreases with thickness over 0.25 in (6 mm)
21.3.2.4 The flux leakage examination referred to in this specification is capable of detecting the presence and location of significant longitudinally or transversely oriented discontinuities However, sensitivity of the test to various types of discontinuities
is affected by the calibration, and different techniques should be employed to detect differently oriented imperfections
21.3.2.5 A purchaser interested in ascertaining the nature (type, size, location, and orientation) of discontinuities that can be detected in the specific application of these examinations should discuss this with the manufacturer of the tubular product
21.3.3 Time of Examination:
21.3.3.1 Nondestructive testing for specification acceptance shall be performed after all mechanical processing, heat treatments, and straightening operations This equipment does not preclude additional testing at earlier stages in the processing
21.3.4 Surface Condition:
21.3.4.1 All surfaces shall be free of scale, dirt, grease, paint, and other foreign material that could interfere with interpretation
of test results The methods used for cleaning and preparing the surfaces for examination shall not be detrimental to the base metal
or the surface finish
21.3.4.2 Excessive surface roughness or deep scratches can produce signals that interfere with the test
21.3.5 Extent of Examination:
21.3.5.1 The relative motion of the pipe and the transducer(s), coil(s), or sensor(s) shall be such that the entire pipe surface is scanned, except as in 21.3.5.2
21.3.5.2 The existence of end effects is recognized, and the extent of such effects shall be determined by the manufacturer, and,
if requested, shall be reported to the purchaser Other nondestructive tests may be applied to the end areas, subject to agreement between the purchaser and the manufacturer
21.3.6 Operator Qualifications:
21.3.6.1 The test unit operator shall be certified in accordance with SNT-TC-1A, or an equivalent recognized and documented standard
21.3.7 Test Conditions:
21.3.7.1 For eddy-current testing, the excitation coil frequency shall be chosen to ensure adequate penetration yet provide good signal-to-noise ratio
21.3.7.2 The maximum eddy-current coil frequency used shall be as follows:
On specified walls up to 0.050 in - 100 kHz max
On specified walls up to 0.150 in - 50 kHz max
On specified walls equal to or greater than 0.150 in - 10 kHz max
21.3.7.3 Ultrasonic—For examination by the ultrasonic method, the minimum nominal transducer frequency shall be 2.00 MHz
and the maximum nominal transducer size shall be 1.5 in
21.3.7.4 If the equipment contains a reject notice filter setting, this shall remain off during calibration and testing unless linearity can be demonstrated at the setting
21.3.8 Reference Standards:
Trang 821.3.8.1 Reference standards of convenient length shall be prepared from a length of pipe of the same grade, size (NPS, or outside diameter and schedule or wall thickness), surface finish and heat treatment conditions as the pipe to be examined
21.3.8.2 For Ultrasonic Testing, the reference ID and OD notches shall be any one of the three common notch shapes shown
in Practice E 213, at the option of the manufacturer The depth of each notch shall not exceed 121⁄2% of the specified wall thickness
of the pipe or 0.004 in [0.1 mm], whichever is greater The width of the notch shall not exceed twice the depth Notches shall be placed on both the OD and ID surfaces
21.3.8.3 For Eddy-Current Testing, the reference standard shall contain, at the option of the manufacturer, any one of the
following discontinuities:
21.3.8.4 Drilled Hole —The reference standard shall contain three or more holes, equally spaced circumferentially around the
pipe and longitudinally separated by a sufficient distance to allow distinct identification of the signal from each hole The holes shall be drilled radially and completely through the pipe wall, with care being taken to avoid distortion of the pipe while drilling One hole shall be drilled in the weld, if visible Alternately, the producer of welded pipe may choose to drill one hole in the weld and run the calibration standard through the test coils three times with the weld turned at 120° on each pass The hole diameter shall be no larger than as follows:
21.3.8.5 Transverse Tangential Notch—Using a round tool or a file with a1⁄4in [6.4 mm] diameter, a notch shall be filed or milled tangential to the surface and transverse to the longitudinal axis of the pipe Said notch shall have a depth not exceeding 12
1⁄2% of the specified wall thickness of the pipe or 0.004 in [0.10 mm], whichever is greater
21.3.8.6 Longitudinal Notch—A notch of 0.031 in [0.8 mm] or less in width shall be machined in a radial plane parallel to the
tube axis on the outside surface of the pipe, to have a depth not exceeding 121⁄2 % of the specified wall thickness of the pipe or 0.004 in [0.10 mm], whichever is greater
21.3.8.7 More or smaller reference discontinuities, or both, may be used by agreement between the purchaser and the manufacturer
21.3.9 Standardization Procedure:
21.3.9.1 The test apparatus shall be standardized at the beginning and end of each series of pipes of the same size (NPS or diameter and schedule or wall thickness), grade and heat treatment condition, and at intervals not exceeding 4 h More frequent standardization may be performed at the manufacturer’s option and may be required upon agreement between the purchaser and the manufacturer
21.3.9.2 The test apparatus shall also be standardized after any change in test system settings, change of operator, equipment repair, or interruption due to power loss, process shutdown or when a problem is suspected
21.3.9.3 The reference standard shall be passed through the test apparatus at the same speed and test system settings as the pipe
to be tested
21.3.9.4 The signal-to-noise ratio for the reference standard shall be 21⁄2 to 1 or greater Extraneous signals caused by identifiable causes such as dings, scratches, dents, straightener marks, etc., shall not be considered noise The rejection amplitude shall be adjusted to be at least 50 % of full scale of the readout display
21.3.9.5 If upon any standardization, the rejection amplitude has decreased by 29 % (3 dB) of peak height from the last standardization, the pipe tested since the last calibration shall be rejected The test system settings may be changed, or the transducer(s), coil(s) or sensor(s) adjusted, and the unit restandardized, but all pipe tested since the last acceptable standardization must be retested for acceptance
21.3.10 Evaluation of Imperfections:
21.3.10.1 Pipes producing a signal equal to or greater than the lowest signal produced by the reference standard(s) shall be identified and separated from the acceptable pipes The area producing the signal may be reexamined
21.3.10.2 Such pipes shall be rejected if the test signal was produced by imperfections that cannot be identified or was produced
by cracks or crack-life imperfections These pipes may be repaired when such repair is permitted by the applicable product specification To be accepted, a repaired pipe must pass the same nondestructive test by which it was rejected, and it must meet the minimum wall thickness requirements of the applicable product specification
21.3.10.3 If the test signals were produced by visual imperfections such as: scratches; surface roughness; dings; straightener marks; cutting chips; steel die stamps; stop marks, or pipe reducer ripple The pipe may be accepted based on visual examination provided that the imperfection is less than 0.004 in [0.1 mm] or 121⁄2 % of the specified wall thickness, whichever is greater 21.3.10.4 Rejected pipe may be reconditioned and retested providing that the wall thickness is not decreased to less than that required by the applicable product specification The outside diameter at the point of grinding may be reduced by the amount so removed To be accepted, retested pipe shall meet the test requirement
21.3.10.5 If the imperfection is explored to the extent that it can be identified as non-rejectable, the pipe may be accepted without further test provided that the imperfection does not encroach on the minimum required wall thickness
Trang 922 Inspection
22.1 The inspector representing the purchaser shall have entry at all times work on the contract of the purchaser is being performed, to all parts of the manufacturer’s works that concern the manufacture of the material ordered The manufacturer shall afford the inspector all reasonable facilities to satisfy him that the material is being furnished in accordance with this specification All required tests and inspection shall be made at the place of manufacture prior to shipment, unless otherwise specified, and shall
be conducted so as not to interfere unnecessarily with operation of the works
23 Rejection
23.1 Each length of pipe received from the manufacturer may be inspected by the purchaser and, if it does not meet the requirements of the specification based on the inspection and test method as outlined in the specification, the length may be rejected and the manufacturer shall be notified Disposition of rejected pipe shall be a matter of agreement between the manufacturer and the purchaser
23.2 Pipe that fails in any of the forming operations or in the process of installation and is found to be defective shall be set aside and the manufacturer shall be notified for mutual evaluation of the suitability of the pipe Disposition of such pipe shall be matter for agreement
24 Certified Test Report
24.1 When specified in the purchase order or contract, the producer or supplier shall furnish a certified test report certifying that the material was manufactured, sampled, tested, and inspected in accordance with the specification, including year date, the supplementary requirements, and any other requirements designated in the purchase order or contract, and the results met the requirements of that specification, the supplementary requirements and the other requirements A signature or notarization is not required on the certified test report, but the document shall be dated and shall clearly identify the organization submitting the report (See Note 4.)
N OTE 4—Notwithstanding the absence of a signature or notarization, the organization submitting the Report is responsible for the contents of the report.
24.2 In addition, the certified test report shall include the following information and test results, when applicable:
24.2.1 Heat number,
24.2.2 Heat analysis,
24.2.3 Product analysis if specified or required,
24.2.4 Tensile properties,
24.2.5 Width in the gage length, when longitudinal strip tension test specimens are used,
24.2.6 Bend test acceptable,
24.2.7 Flattening test acceptable,
24.2.8 Hydrostatic test pressure,
24.2.9 Nondestructive electric test pressure,
24.2.10 Impact test results, and
24.2.11 Other test results or information required to be reported by the product specification
24.3 Test results or information required to be reported by supplementary requirements, or other requirements designated in the purchase order or contract shall be reported but may be reported in a separate document
24.4 The certified test report shall include a statement of explanation for the letter added to the specification number marked
on the tubes (see 25.5) when all of the requirements of the specification have not been completed The purchaser must certify that all requirements of the specification have been completed before the removal of the letter (that is, X, Y, or Z)
24.5 A material test report, certificate of inspection, or similar document printed from or used in electronic form from an electronic data interchange (EDI) transmission shall be regarded as having the same validity as a counterpart printed in the certifier’s facility The content of the EDI transmitted document shall meet the requirements of the invoked ASTM standard(s) and conform to any existing EDI agreement between the purchaser and supplier Notwithstanding the absence of a signature, the organization submitting the EDI transmission is responsible for the content of the report
25 Product Marking
25.1 Each length of pipe shall be legibly marked with the manufacturer’s name or brand, the specification number (year of issue not required) and grade Marking shall begin approximately 12 in [300 mm] from the end of each length of pipe For pipe less than NPS 2 and pipe under 3 ft [1 m] in length, the required information may be marked on a tag securely attached to the bundle
or box in which the pipes are shipped
25.2 When pipe marked as specified is rejected, the ASTM designation shall be canceled
25.3 For austenitic steel pipe, the marking paint or ink shall not contain detrimental amounts of harmful metals, or metal salts, such as zinc, lead, or copper, which cause corrosive attack on heating
25.4 Pipes that have been weld repaired in accordance with 16.1 shall be marked WR
25.5 When it is specified that certain requirements of a specification adopted by the ASME Boiler and Pressure Vessel Committee are to be completed by the purchaser upon receipt of the material, the manufacturer shall indicated that all requirements
Trang 10of the specification have not been completed by a letter such as X, Y, or Z, immediately following the specification number This letter may be removed after completion of all requirements in accordance with the specification An explanation of specification requirements to be completed is provided in 24.1
26 Packaging, Marking, and Loading
26.1 When specified on the purchase order, packaging, marking, and loading for shipment shall be in accordance with the procedures of Practices A 700
27 Government Procurement
27.1 When specified in the contract or order, the following requirements shall be considered in the inquiry, contract, or order for agencies of the U.S Government where scale-free pipe is required These requirements shall take precedence if there is a conflict between these requirements and the product specification
27.2 Pipe shall be ordered to nominal pipe size (NPS) and schedule Nominal pipe shall be as specified in ANSI B36.10
27.3 Responsibility for Inspection—Unless otherwise specified in the contract or purchase order, the manufacture is responsible
for the performance of all inspection and test requirements specified The absence of any inspection requirements in the specification shall not relieve the contractor of the responsibility for ensuring that all products or supplies submitted to the government for acceptable comply with all requirements of the contract Sampling inspection, as part of the manufacturing operations, is an acceptable practice to ascertain conformance to requirements, however, this does not authorize submission of known defective material, either indicated or actual, nor does it commit the government to accept the material Except as otherwise specified in the contract or purchase order, the manufacturer may use his own or any other suitable facilities for the performance
of the inspection and test requirements unless disapproved by the purchaser at the time the order is placed The purchaser shall have the right to perform any of the inspections and tests set forth when such inspections and tests are deemed necessary to ensure that the material to conforms to the prescribed requirements
27.4 Sampling for Flattening and Flaring Test and for Visual and Dimensional Examination—Minimum sampling for flattening
and flaring tests and visual and dimensional examination shall be as follows:
In all cases, the acceptance number is zero and the rejection number is one Rejected lots may be screened and resubmitted for visual and dimensional examination All defective items shall be replaced with acceptable items prior to lot acceptance
27.5 Sampling for Chemical Analysis—One sample for chemical analysis shall be selected from each two pipes chosen from
each lot A lot shall be all material poured from one heat
27.6 Sampling for Tension and Bend Test—One sample shall be taken from each lot A lot shall consist of all pipe of the same
outside diameter and wall thickness manufactured during an 8-h shift from the same heat of steel, and heat treated under the same conditions of temperature and time in a single charge in a batch type furnace, or heat treated under the same condition in a continuous furnace, and presented for inspection at the same time
27.7 Hydrostatic and Ultrasonic Tests—Each pipe shall be tested by the ultrasonic (when specified) and hydrostatic tests.
27.8 Pipe shall be free from heavy oxide or scale The internal surface of hot finished ferritic steel pipe shall be pickled or blast cleaned to a free of scale condition equivalent to the CSa2 visual standard in SSPC-SP6 Cleaning shall be performed in accordance with a written procedure that has been shown to be effective This procedure shall be available for audit
27.9 In addition to the marking required by this specification, each length of pipe NPS 1⁄4 or larger shall be marked, in accordance with FED-STD-183 and MIL-STD-792, with the nominal pipe size, schedule number, length, and heat number or lot identification number
27.10 Pipe shall be straight to within the tolerance in Table 2
27.11 When specified, each pipe shall be ultrasonically examined in accordance with MIL-STD-271, except that the notch depth
in the calibration standard shall be 5 % of the wall thickness or 0.005 in [0.1 mm], whichever is greater Any pipe that produces
an indication equal to or greater than 100 % of the indication from the calibration standard shall be rejected
27.12 The pipe shall be free from repair welds, welded joints, laps, laminations, seams, visible cracks, tears, grooves, slivers, pits, and other imperfections detrimental to the pipe as determined by visual and ultrasonic examination, or alternate tests, as specified
27.13 Pipe shall be uniform in quality and condition and have a finish conforming to the best practice for standard quality pipe Surface imperfections such as handling marks, straightening marks, light mandrel and die marks, shallow pits, and scale pattern will not be considered injurious if the imperfections are removable within the tolerances specified for wall thickness or 0.005 in [0.1 mm], whichever is greater The bottom of imperfections shall be visible and the profile shall be rounded and faired-in