High Cycle Fatigue: A Mechanics of Materials Perspective part 8 ppsx

For purposes of presenting the equation in the form of a Haigh diagram, the stress limits are written in terms of mean and alternating stresses 2 case of uniaxial loading, the following

0 0.5

1

Haigh equation

k1=1.0, k2= 0.0

σmean /σult

σalt

σult

Figure 2.30. Constant life diagram for parabolic equation of Haigh.



 





(2.15b)

where e and g are either positive or negative constants Because of the large number of terms, most experimentally determined constant life data may be represented by proper selection of the constants

2.8 JASPER EQUATION

Of both practical and historical significance is the observation that Jasper [32], in 1923, proposed that fatigue life is related to the stored energy density range per cycle in

a material when evaluating data obtained earlier by Haigh Applying this concept to HCF conditions, it can be assumed that all stresses and strains are elastic, thus all equations represent purely elastic behavior For purely uniaxial loading, the shaded area

in Figure 2.31 illustrates schematically the stored energy for the cases where loading is purely tensile R > 0 The energy for the case where R < 0, which involves tension and compression in a single cycle, is illustrated in Figure 2.32 by the shaded area The stored energy density range per cycle is then given for uniaxial loading by

E

max min

σ

ε

Figure 2.31. Stored energy (shaded) for elastic loading under tension fatigue R > 0.

min

max

σ

ε

Figure 2.32. Stored energy (shaded) for elastic loading under reversed fatigue R < 0.

2.32) For purposes of presenting the equation in the form of a Haigh diagram, the stress limits are written in terms of mean and alternating stresses

2

case of uniaxial loading, the following equation is easily derived and can be used to obtain the value of the alternating stress on a Haigh diagram in terms of stress ratio, R:

2

Of interest is the shape of the Haigh diagram corresponding to a constant energy density range for any positive mean stress value Such a diagram is shown in Figure 2.33 which has the same general shape as that for Ti-6Al-4V bar material (Figure 2.34) obtained

is required to describe the values on both the x and y axes This plot (Figure 2.33) is the same type as shown previously as the Jasper equation in Figure 2.28, using typical numbers for titanium plate, where the alternating stresses corresponding to negative mean stresses are also included

Data on another high strength titanium alloy, Ti-6-2-4-6, that extend into the negative mean stress regime are shown in Figure 2.35 These data show the same general trend

as the Jasper equation curve of Figure 2.33 for positive mean stresses and have a shape

0 0.2 0.4 0.6 0.8 1 1.2

σalt

σ–1

σmean /σ–1

Normalized Haigh diagram Jasper equation

Figure 2.33. Normalized Haigh diagram representing Jasper equation for positive mean stresses.

0 100 200 300 400 500 600 700 800

Mean stress (MPa)

Ti-6Al-4V bar

10 7 cycles

70 Hz

Figure 2.34. Haigh diagram for Ti-6Al-4V bar [33].

similar to that shown subsequently in Figure 2.36 when extended into the negative mean stress regime The representation of data for negative mean stresses is discussed in the following paragraphs

Experimental data for negative mean stress were obtained by Nicholas and Maxwell [29] that showed they neither followed the Jasper equation nor the SWT or Walker equations (see Figure 2.28) For that reason, they proposed a modification to the Jasper equation that treats the stored energy due to tension differently than that due to com-pression stresses Haigh [30], in 1929, in referring to Bauschinger’s results from 1915

0 100 200 300 400

Mean stress (MPa)

10 7 cycles 60–70 Hz

Figure 2.35. Haigh diagram for Ti-6-2-4-6.

0 100 200 300 400 500 600 700 800

ML data ASE data Jasper, α= 0.287

Mean stress (MPa)

Ti-6Al-4V plate

10 7 cycles 20–70 Hz

Figure 2.36. Haigh diagram for Ti-6Al-4V plate including modified Jasper equation fit.

and 1917, noted that “this series of tests    was probably the first that ever revealed

data on naval brass, he indicated, “In this metal, as in many others, pull tends to reduce the fatigue limit while push increases the resistance to fatigue.” Following this idea, Nicholas and Maxwell postulated that stored energy density per cycle does not contribute

∗

“Push” and “pull” was the common nomenclature for tension and compression, respectively, in that time period.

towards the fatigue process as much when the stresses are compressive as when they are

in tension Taking the simplest approach, where compressive stress energy contributes

In the use of this equation, energy terms corresponding to negative stresses have to modifying the shape of the Jasper equation as shown in Figure 2.37 for several values of

−1 corresponding to negative mean stresses

Using the Ti-6Al-4V forged plate material, fatigue tests were conducted under constant

mini-mum stress ratio value at which tests could be conducted was limited by the compressive yield strength of the material To establish the fatigue limit strength corresponding to

Nicholas [33] that is discussed in the next chapter

The experimental values for the FLS obtained for a broad range of values of R are plotted in the form of a Haigh diagram in Figure 2.36 The data are shown as ML in the figure, and are combined with previously unpublished data from Allied Signal Engines (ASE), now Honeywell, on the same material A best fit of the data using the modified equation (2.22) was obtained as 0.287 by fitting to the experimental data obtained from

0 100 200 300 400 500 600

α = 1

α = 0.75

α= 0.5

α= 0.25

Mean stress

Constant life diagram modified Jasper

Figure 2.37.

In reviewing the methods for representing fatigue limit data on constant life diagrams, Maxwell and Nicholas [33] noted that the Haigh diagram is the one that has achieved the most popularity In a review of these diagrams, the authors suggested that the most important information for design was not only the alternating stress, but also the maximum stress, as represented in a plot against mean stress (see Figures 2.20 and 2.21 above)

To this end, a diagram called the Nicholas–Haigh diagram was proposed [33] which, as history would note, received absolutely no acceptance or recognition from the technical community and was short-lived, never to be mentioned again until here For the sake

of posterity, the reasoning behind the proposed diagram, and more importantly, the importance of maximum stress in constant life diagrams is discussed next

The plot of both alternating stress and maximum stress against mean stress, initially referred to as a Nicholas–Haigh diagram [33] is presented at the possible expense of duplicating past efforts as well as confusing future historians This plot can be used

to present data for engineering design in two fashions For low values of mean stress

or low R R < 05, the alternating stress is the crucial allowable quantity, particularly for rotating machinery applications where mean stresses are relatively predictable and normally are well defined For high values of mean stress or high R R > 05, maximum stress becomes the more critical parameter in design It is suggested here that margins of safety be imposed on both parameters (alternating stress and maximum stress) in order

to insure a safe design The Nicholas–Haigh diagram was an attempt to present data in a form that would allow a designer to recognize the importance of both quantities Such a plot may not be totally new, but the following features were incorporated in it:

intended or implied to represent the data

is related to any material property such as yield or ultimate stress

This last condition differs from most previous diagrams or laws that attempt to pin the data to the ultimate strength for theoretical reasons, or to yield stress for engineering purposes One of the main reasons for avoiding an intercept such as the ultimate strength

is that ultimate strength depends on the strain rate at which a test is conducted, and since most metals exhibit some degree of strain-rate hardening [34] Data plotted on a

Nicholas-Haigh diagram are normally conducted at a single frequency which produces a different strain rate for each different amplitude of alternating stress For increasing values

of mean stress, as R approaches 1, the strain rate approaches zero since the alternating stress amplitude is normally found to decrease in this region This is equivalent to having

a cyclic stress–strain curve near the ultimate stress at an arbitrarily slow rate of loading Thus, a fourth condition can be suggested for a completely defined Nicholas–Haigh diagram, namely, that the frequency of loading for all data points be specified on the diagram

It should be noted that data for Haigh or other constant life diagrams for large cycle

Thus, the strain rates associated with such tests are not quasi static For this reason, maximum stress values obtained under fatigue testing at high values of R and high frequency can often be above the quasi-static ultimate strength of the material This, in turn, will not produce a smooth plot on a Haigh diagram if a quasi-static ultimate strength

is used to anchor the plot to the x-axis

As a further consideration, it is recommended that all data points be included,

to exhibit creep behavior which may lead to a creep rather than a fatigue failure (see the discussion in Chapter 3 on testing at high stress ratios as well as the earlier discussion

on Haigh diagrams at elevated temperature) Nonetheless, if the frequency is specified, the time to failure can be easily deduced Data of this type should be appended with a footnote if necessary, but they are still valid design data, even though the mode of failure

is not pure fatigue

In the limit, a “fatigue” test at very high values of R becomes a creep or sustained load test Any strain hardening which occurs due to strain rate effects, therefore, is influenced

by the rate of loading which is used in going from zero to mean stress during the first half cycle at the start of the test This rate of loading should be recorded, particularly if data are to be compared with an ultimate stress value The ultimate stress, consequently, should be obtained from a test at the same rate of loading for consistency

An example of a Nicholas–Haigh diagram is presented in Figure 2.38 for titanium alloy Ti-6Al-4V The data are those presented previously in Figure 2.36 and are represented

by the modified Jasper equation for both maximum and alternating stress Note that the maximum stress approaches and then exceeds the yield stress of the material (930 MPa)

at high values of mean stress

It is of importance to note that the Haigh diagram, especially when extended into the negative mean stress regime, provides useful information on the potential beneficial effects of residual stresses (Residual stresses and their role in endurance limits are discussed in detail in Chapter 8.) Notwithstanding the fact that stress gradients play an important role in fatigue, comparing allowable alternating stresses as a function of mean stress can give guidance on the role that residual stress can play in altering the fatigue

0 200 400

ML data ASE data

Mean stress (MPa)

Ti-6Al-4V plate

10 7 cycles 20–70 Hz

Figure 2.38. Nicholas–Haigh diagram for Ti-6Al-4V plate with modified Jasper equation fit shown for

alter-nating stress (solid line) and maximum stress (dashed line).

limit strength Noting again that compressive residual stresses do not alter the range of stress or alternating stress applied to a material or structure but, rather, reduce the mean stress, the Haigh diagram provides data on the reduction of the allowable alternating stress as a function of mean stress Using the Jasper equation as a measure of the

2, as

residual stress is added, then the modified Jasper diagram representing Ti-6Al-4V plate material, Figure 2.36 shows that the benefit of compressive residual stress is somewhat

Figure 2.36 indicates a benefit in allowable alternating stress of only approximately 20% since the alternating stress of approximately 500 MPa only increases to approximately

600 MPa This type of information can be easily seen in a plot of maximum stress against mean stress, Figure 2.38, where the maximum stress corresponding to the fatigue limit

is seen to decrease as mean stress decreases in the negative mean stress regime Thus, it has to be ascertained where the mean stress is without residual stress and where the mean stress will be after a compressive residual stress is developed From that information, the allowable alternating stress for the material can be determined and the benefit of the residual stress ascertained The subject of residual stresses and their effect on fatigue behavior in conjunction with other considerations evolving from surface treatments is discussed further in Chapter 8

2.9. OBSERVATIONS ON STEP TESTS AT NEGATIVE R

Data obtained in [29] have been examined for implications on the initiation and subsequent propagation of cracks in smooth bars cycled at negative stress ratios The data, shown above in a Haigh diagram in Figure 2.38, cover a range of stress ratios, R, from a high

which accounts for the different behavior in initiation in compression compared to that

in tension using the constant  In addition to the alternating stress normally provided in

a Haigh diagram, the maximum stress is also shown by a dashed line in the figure The data were obtained using the step-loading procedure, described in the next chapter, with

block as a function of R shown in Figure 2.39 The relatively low number of cycles in the last block leads to speculation that these specimens, at low values of R, had already developed cracks in earlier cycle blocks and that these cracks did not propagate until some higher stress level was reached in the final block If, according to this speculation, the crack propagates only due to positive stresses (positive K), then the cracks formed

at lower values of R must be larger than those at higher R because the maximum stress (positive portion of cycle) decreases with decreasing R (see Figure 2.38) The indirect evidence of small numbers of cycles in the last loading block is discussed further in Chapter 3 when dealing with specimens that are deliberately precracked before endurance limits are determined using step loading

The speculation about crack initiation and subsequent propagation at negative R can

be explained with the aid of Figure 2.40, where the conditions for initiation compared

to propagation are shown schematically The initiation of a crack, if associated with the

ML data ASE data

Stress ratio, R

Ti-6Al-4V plate Smooth bar step tests

10 7 cycle blocks

60 Hz

Figure 2.39. Cycles to failure in last cycle block for smooth bar specimens.

ML data ASE data Jasper, α= 0. 287

Mean stress (MPa)

Ti-6Al-4V plate

10... on a